Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Limiting oxygen index | 23.0 °C | 46 % Show Supplier Material materials with Limiting oxygen index of 46 % | |
Relative density | 23.0 °C | 1.42 [-] Show Supplier Material materials with Relative density of 1.42 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 1 % Show Supplier Material materials with Water absorption of 1 % | ISO 62-1 | (23°C/saturated) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 6.8 GPa Show Supplier Material materials with Elastic modulus of 6.8 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 6.5 GPa Show Supplier Material materials with Flexural modulus of 6.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 210 MPa Show Supplier Material materials with Flexural strength of 210 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 90 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 90 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 480 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 480 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 140 MPa Show Supplier Material materials with Tensile strength of 140 MPa | ISO 527 | break, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature | 205 - 210 °C Show Supplier Material materials with Heat deflection temperature of 205 - 210 °C | ||||
Heat deflection temperature, 0.45 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 170 °C Show Supplier Material materials with Relative temperature index, electrical of 170 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 170 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | |||
Vicat softening temperature | 212 °C Show Supplier Material materials with Vicat softening temperature of 212 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating: ≥1.9mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221093- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=502535- - | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor | 23.0 °C | 4.9E-3 [-] Show Supplier Material materials with Dissipation factor of 4.9E-3 [-] | IEC 60250 | 2450 MHz |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Shrinkage | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronics | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Maximum Moisture Content: 0.02% | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |