ULTEM™ Resin 2300F - Americas

Want to keep this datasheet? Save it now in your required format

Description

30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.

Ashby charts

See where ULTEM™ Resin 2300F - Americas falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

1.51 g/cm³ at 23 °C

ISO 1183

Limiting oxygen index

LOI

50 % at 23 °C

Moisture absorption

cmoisture

0.5 % at 23 °C

ISO 62 | (23°C / 50% RH)

Relative density

ρrel

1.51 [-] at 23 °C

ASTM D 792 |

Water absorption

cwater

0.9 % at 23 °C

ISO 62-1 | (23°C/saturated)

Mechanical

Elastic modulus

E

9.5 GPa at 23 °C

Show Polyetherimide (PEI) materials with Elastic modulus of 9.5 GPa at 23 °C

ISO 527 | 1 mm/min

Elongation

A

2 % at 23 °C

Show Polyetherimide (PEI) materials with Elongation of 2 % at 23 °C

ISO 527 | yield, 5 mm/min

Flexural modulus

Ebend

8.5 GPa at 23 °C

Show Polyetherimide (PEI) materials with Flexural modulus of 8.5 GPa at 23 °C

ISO 178 | 2 mm/min

Flexural strength

σbend

225 MPa at 23 °C

Show Polyetherimide (PEI) materials with Flexural strength of 225 MPa at 23 °C

ISO 178 | yield, 2 mm/min

Hardness, Ball Indentation

HBI

165 MPa at 23 °C

Show Polyetherimide (PEI) materials with Hardness, Ball Indentation of 165 MPa at 23 °C

ISO 2039-1 | H358/30

Hardness, Rockwell M

HRM

114 [-] at 23 °C

Show Polyetherimide (PEI) materials with Hardness, Rockwell M of 114 [-] at 23 °C

ASTM D 785 |

Impact strength, Charpy notched

Ivnot

10 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Charpy notched of 10 kJ/m² at 23 °C

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Charpy unnotched

Iunnot

40 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Charpy unnotched of 40 kJ/m² at 23 °C

ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod notched

IIzod,not

40 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod notched of 40 kJ/m² at 23 °C

ISO 180/1A | notched 80*10*4, -30°C

Impact strength, Izod notched, ASTM

IIzod,not,astm

85 J/m at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod notched, ASTM of 85 J/m at 23 °C

ASTM D 256

Impact strength, Izod unnotched

IIzod,unnot

40 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod unnotched of 40 kJ/m² at 23 °C

ISO 180/1U | unnotched 80*10*4, -30°C

Impact strength, Izod unnotched, ASTM

IIzod,unnot,astm

427 J/m at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod unnotched, ASTM of 427 J/m at 23 °C

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

ItotalE

10 J at 23 °C

Show Polyetherimide (PEI) materials with Instrumented Impact, Total Energy of 10 J at 23 °C

ASTM D 3763 | 23°C

Taber Abrasion

TA

20 mg/1000cy at 23 °C

Show Polyetherimide (PEI) materials with Taber Abrasion of 20 mg/1000cy at 23 °C

SABIC method | CS-17, 1 kg

Tensile strength

Rm

165 MPa at 23 °C

Show Polyetherimide (PEI) materials with Tensile strength of 165 MPa at 23 °C

ISO 527 | yield, 5 mm/min

Thermal

Ball Pressure Test

nan

Coefficient of thermal expansion

α

2E-5 1/K at 23 °C

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

αtrans

6E-5 1/K at 23 °C

ISO 11359-2 | 23°C to 150°C

Flammability

UL Recognized, 94-5VA Flame Class Rating: 1.2 mm UL 94 | UL Recognized, 94V-0 Flame Class Rating: 0.25 mm UL 94 | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221099

Glow Wire Ignition Temperature

GWIT

900 °C

IEC 60695-2-13 | 2.0 mm

Heat deflection temperature, 0.45 MPa

HDT0.45,MPa

212 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

HDT1.8,MPa

210 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

RTIel

180 °C

UL 746B

Relative temperature index, mechanical impact

RTIimp

170 °C

UL 746B

Relative temperature index, mechanical strength

RTIstr

180 °C

UL 746B

Thermal conductivity

λ

0.29 W/(m·K) at 23 °C

ISO 8302

Vicat softening temperature

Tsoft

220 °C

ISO 306 | Rate B/120

Electrical

Comparative tracking index

CTI

4 V at 23 °C

UL 746A | (UL) {PLC}

Dielectric constant, 1MHz

εr,1MHz

3.4 [-] at 23 °C

IEC 60250

Dielectric constant, 60Hz

εr,60Hz

3.3 [-] at 23 °C

IEC 60250 | 50/60 Hz

Dielectric strength

EDS

24.8 kV/mm at 23 °C

ASTM D 149 | in air, 1.6 mm

Dissipation factor

ε''

5.3E-3 [-] at 23 °C

ASTM D 150 | 2450 MHz

Dissipation factor, 1MHz

ε''1MHz

2.3E-3 [-] at 23 °C

IEC 60250

Dissipation factor, 1kHz

ε''1KHz

1.5E-3 [-] at 23 °C

ASTM D 150

Dissipation factor, 50Hz

ε''50Hz

1.6E-3 [-] at 23 °C

IEC 60250 | 50/60 Hz

High Amp Arc Ignition

HAI

3 mm at 23 °C

UL 746A | PLC 4

High Volt Arc Track Rate

HVTR

3 PLC Code at 23 °C

UL 746A | (PLC)

Hot-Wire Ignition

HWI

3 mm at 23 °C

UL 746A | PLC 1

Sheet resistivity, ROA

ρel,sheet, ROA

1.00E+15 Ω at 23 °C

IEC 60093

Volume resistivity

ρel, vol

3.00E+16 Ω·cm at 23 °C

ASTM D 257

Rheological Properties

Melt mass-flow rate

MFR

5 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

MVR

6 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Shrinkage

cshrink

0.2 % at 23 °C

SABIC method | on tensile bar

Shrinkage, transverse

cshrink, trans

0.2 % at 23 °C

SABIC method | 3.2 mm

Technological properties

Application areas

Non-LED Lighting, Aerospace, Electronic Components

Availability

Europe,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Food Contact Acceptable

Filler Type

Processing Tag

Processing methods

Back Pressure: 0.3 to 0.7 MPa | Mold Temperature: 135 to 165.0 °C | Maximum Moisture Content: 0.02 % | Vent Depth: 0.025 to 0.076 mm | Nozzle Temperature: 345 to 400.0 °C | Drying Time (Cumulative): 24 hrs | Middle - Zone 2 Temperature: 340 to 400.0 °C | Rear - Zone 1 Temperature: 330 to 400.0 °C | Screw Speed: 40 to 70.0 rpm | Shot to Cylinder Size: 40 to 60.0 % | Melt Temperature: 350 to 400.0 °C | Drying Temperature: 150 °C | Drying Time: 4 to 6.0 hrs | Front - Zone 3 Temperature: 345 to 400.0 °C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.