LNP™ LUBRICOMP™ Compound RCP36 - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.22 - 0.25 [-]

Show Supplier Material materials with Coefficient of friction of 0.22 - 0.25 [-]

Coefficient of friction, kinetic

0.25 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.25 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.22 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.22 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.34 g/cm³

Show Supplier Material materials with Density of 1.34 g/cm³

ISO 1183

Moisture absorption

23.0 °C

1.35 %

Show Supplier Material materials with Moisture absorption of 1.35 %

ISO 62 | (23°C / 50% RH)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

23.1 GPa

Show Supplier Material materials with Elastic modulus of 23.1 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break

Flexural modulus

23.0 °C

21.3 GPa

Show Supplier Material materials with Flexural modulus of 21.3 GPa

ISO 178

Flexural strength

23.0 °C

354 MPa

Show Supplier Material materials with Flexural strength of 354 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

96 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 96 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched

23.0 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 65 kJ/m²

ISO 180/1U | 80*10*4, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

945 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 945 J/m

ASTM D 4812 | 23°C

Instrumented Impact, at Peak

23.0 °C

9 J

Show Supplier Material materials with Instrumented Impact, at Peak of 9 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

228 MPa

Show Supplier Material materials with Tensile strength of 228 MPa

ISO 527 | break

Thermal

PropertyValueComment

Heat deflection temperature

240 - 254 °C

Show Supplier Material materials with Heat deflection temperature of 240 - 254 °C

Heat deflection temperature, 0.45 MPa

254 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 254 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

240 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 240 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Flammability

UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101281618- -

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.15 %

Show Supplier Material materials with Shrinkage of 0.15 %

ISO 294 | 24 hrs

Shrinkage, transverse

23.0 °C

0.43 %

Show Supplier Material materials with Shrinkage, transverse of 0.43 %

ISO 294 | 24 hrs

Technological properties

Property
Application areas

Personal Computing, Weapon, Document Handling, Individual Equiptment, Humidity Control, Exterior Mirror

Availability

Europe,Asia,Americas

Features

Structural, Wear and Friction

Processing methods

Maximum Moisture Content: 0.15 to 0.25%
Middle - Zone 2 Temperature: 280 to 295.0°C
Melt Temperature: 275 to 290.0°C
Front - Zone 3 Temperature: 295 to 305.0°C
Mold Temperature: 80 to 95.0°C
Back Pressure: 0.2 to 0.3MPa
Screw Speed: 30 to 60.0rpm
Drying Time: 4hrs
Rear - Zone 1 Temperature: 265 to 275.0°C
Drying Temperature: 80°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.