Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.24 g/cm³ Show Supplier Material materials with Density of 1.24 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 23 % Show Supplier Material materials with Limiting oxygen index of 23 % | |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.24 [-] Show Supplier Material materials with Relative density of 1.24 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.15 % Show Supplier Material materials with Water absorption of 0.15 % | ISO 62-1 | (23°C/saturated) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 6 GPa Show Supplier Material materials with Elastic modulus of 6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 4.5 GPa Show Supplier Material materials with Flexural modulus of 4.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 135 MPa Show Supplier Material materials with Flexural strength of 135 MPa | ISO 178 | break, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Supplier Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 | H358/30 |
Impact strength, Charpy unnotched | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 25 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 60 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 60 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 25 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 14 J Show Supplier Material materials with Instrumented Impact, Total Energy of 14 J | ASTM D 3763 | 23°C |
Taber Abrasion | 23.0 °C | 45 mg/1000cy Show Supplier Material materials with Taber Abrasion of 45 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | ISO 527 | break, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Ball pressure temperature | 165 °C Show Supplier Material materials with Ball pressure temperature of 165 °C | IEC 60695-10-2 | approximate maximum | |||
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature | 160 - 170 °C Show Supplier Material materials with Heat deflection temperature of 160 - 170 °C | ||||
Heat deflection temperature, 0.45 MPa | 170 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 170 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Thermal conductivity | 23.0 °C | 0.26 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.26 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 180 °C Show Supplier Material materials with Vicat softening temperature of 180 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236755- - | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 200 V Show Supplier Material materials with Comparative tracking index of 200 V | IEC 60112 | |
Dielectric constant, 1MHz | 23.0 °C | 2.6 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.6 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.7 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1MHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 6E-3 [-] | IEC 60250 | 50/60 Hz |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 4.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 4.5 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Melt volume-flow rate | 11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Freezer, Electrical, EV/HEV Battery, Industrial Material Handling, Heavy Vehicles, Hot Water System, Electronic Components, Enclosures, Auto Aftermarket, Cooking Range, Washing Machine, Underhood, Wiring Devices, Wireless Communications, Pump, Ignition System, Microwave Oven, Motorcycle, Personal Computing | |
| Availability | Europe | |
| Processing methods | Mold Temperature: 80 to 120.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |