LEXAN™ Copolymer EXL9132 - Americas

Want to keep this datasheet? Save it now in your required format

Description

Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temperature ductility, UV stabilized. Non-chlorinated, non-brominated flame retardant product. UL rated V0/5VA.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Electrical Engineering

Electronics

Display Devices

Construction

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.15 % Show Supplier Material materials with Moisture absorption of 0.15 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.18 [-] Show Supplier Material materials with Relative density of 1.18 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.35 % Show Supplier Material materials with Water absorption of 0.35 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	100 % Show Supplier Material materials with Elongation of 100 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	88 MPa Show Supplier Material materials with Flexural strength of 88 MPa	ISO 178 \| yield, 2 mm/min
Hardness, Ball Indentation	23.0 °C	95 MPa Show Supplier Material materials with Hardness, Ball Indentation of 95 MPa	ISO 2039-1 \| H358/30
Impact strength, Charpy notched	23.0 °C	60 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 60 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	20 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m²	ISO 180/1A \| notched 80103, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	560 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 560 J/m	ASTM D 256 \| notched, -30°C
Instrumented Impact, Total Energy	23.0 °C	67 J Show Supplier Material materials with Instrumented Impact, Total Energy of 67 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	55 MPa Show Supplier Material materials with Tensile strength of 55 MPa	ISO 527 \| break, 50 mm/min
Impact strength, Charpy unnotched	ISO 179/1eU \| Unnotch Edgew 80103 sp=62mm, -30°C
Impact strength, Izod unnotched	ISO 180/1U \| 80103, 23°C

Thermal

Property	Temperature	Value	Comment
Ball Pressure Test		nan	IEC 60695-10-2 \| 125°C +/- 2°C
Coefficient of thermal expansion	23.0 °C	7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.5E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Coefficient of thermal expansion, transverse	23.0 °C	7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		124 - 136 °C Show Supplier Material materials with Heat deflection temperature of 124 - 136 °C
Heat deflection temperature, 0.45 MPa		136 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 136 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Vicat softening temperature		144 °C Show Supplier Material materials with Vicat softening temperature of 144 °C	ISO 306 \| Rate B/120

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	3 V Show Supplier Material materials with Comparative tracking index of 3 V	UL 746A \| (UL) {PLC}
Dielectric constant, 1MHz	23.0 °C	2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-]	IEC 60250
Dielectric constant, 60Hz	23.0 °C	2.7 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.7 [-]	IEC 60250 \| 50/60 Hz
Dielectric strength	23.0 °C	19 kV/mm Show Supplier Material materials with Dielectric strength of 19 kV/mm	IEC 60243-1 \| in oil, 3.2 mm,
Dissipation factor, 1MHz	23.0 °C	0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-]	IEC 60250
Dissipation factor, 50Hz	23.0 °C	4E-4 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 4E-4 [-]	IEC 60250 \| 50/60 Hz

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		17 g/10min Show Supplier Material materials with Melt mass-flow rate of 17 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		16 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 16 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Security/Detection, Medical Facility Infrastructure, Wireless Communications, Washing Machine, Electronic Components, Enclosures, Data Transfer, Animal Testing, Circuit Protection
Availability	Europe,Asia,Americas
Processing methods	Front - Zone 3 Temperature: 295 to 315.0°C Melt Temperature: 295 to 315.0°C Drying Time (Cumulative): 48hrs Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm Mold Temperature: 70 to 95.0°C Middle - Zone 2 Temperature: 280 to 305.0°C Drying Temperature: 120°C Screw Speed: 40 to 70.0rpm Rear - Zone 1 Temperature: 270 to 295.0°C Drying Time: 3 to 4.0hrs Back Pressure: 0.3 to 0.7MPa Nozzle Temperature: 290 to 310.0°C Maximum Moisture Content: 0.02%
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.