Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.1 GPa Show Supplier Material materials with Elastic modulus of 10.1 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 1.8 % Show Supplier Material materials with Elongation of 1.8 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 8.1 GPa Show Supplier Material materials with Flexural modulus of 8.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 169 MPa Show Supplier Material materials with Flexural strength of 169 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 76 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 76 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 76 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 76 J/m | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 148 MPa Show Supplier Material materials with Tensile strength of 148 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.43E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.43E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.5E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Heat deflection temperature | 203 °C Show Supplier Material materials with Heat deflection temperature of 203 °C | ||||
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102158299- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15.4 g/10min Show Supplier Material materials with Melt mass-flow rate of 15.4 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Melt volume-flow rate | 34 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 34 cm³/10min | ISO 1133 | MVR at 345°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.53 % Show Supplier Material materials with Shrinkage, transverse of 0.53 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Semiconductor | |
Availability | Asia | |
Processing methods | Melt Temperature: 350 to 400.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |