General
Property | Temperature | Value |
---|---|---|
Limiting oxygen index | 23.0 °C | 48 % Show Supplier Material materials with Limiting oxygen index of 48 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 10 % Show Supplier Material materials with Elongation of 10 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 4.4 GPa Show Supplier Material materials with Flexural modulus of 4.4 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 144 MPa Show Supplier Material materials with Flexural strength of 144 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Taber Abrasion | 23.0 °C | 11 mg/1000cy Show Supplier Material materials with Taber Abrasion of 11 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Tensile strength | 23.0 °C | 96 MPa Show Supplier Material materials with Tensile strength of 96 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.5E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 4.86E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.86E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Heat deflection temperature | 214 °C Show Supplier Material materials with Heat deflection temperature of 214 °C | ||||
Heat deflection temperature, 1.80 MPa | 214 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 214 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Vicat softening temperature | 237 °C Show Supplier Material materials with Vicat softening temperature of 237 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221112- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 20.8 kV/mm Show Supplier Material materials with Dielectric strength of 20.8 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Americas | |
Processing methods | Drying Time: 4 to 6.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |