General
Property | Temperature | Value |
---|---|---|
Limiting oxygen index | 23.0 °C | 48 % Show Supplier Material materials with Limiting oxygen index of 48 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 3.8 GPa Show Supplier Material materials with Flexural modulus of 3.8 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 150 MPa Show Supplier Material materials with Flexural strength of 150 MPa | ISO 178 | yield, 2 mm/min |
Taber Abrasion | 23.0 °C | 35 mg/1000cy Show Supplier Material materials with Taber Abrasion of 35 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.5E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature | 202 °C Show Supplier Material materials with Heat deflection temperature of 202 °C | ||||
Heat deflection temperature, 1.80 MPa | 202 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 202 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Vicat softening temperature | 222 °C Show Supplier Material materials with Vicat softening temperature of 222 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221112- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 17 kV/mm Show Supplier Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, IEC 60093 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Americas | |
Processing methods | Melt Temperature: 370 to 410.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |