VALOX™ FR Resin ENH8560 - Europe

Want to keep this datasheet? Save it now in your required format

Description

VALOX ENH8560 is a 30% glass reinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate/Polyethylene Terephthalate (PBT/PET) injection moldable grade with excellent chemical resistance. It has a UL94V0@1.5mm and 5VA@3.0mm flame rating. This is a good candidate for a variety of applications needing a sustainable FR PBT/PET solution.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.58 g/cm³

Show Supplier Material materials with Density of 1.58 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

31 %

Show Supplier Material materials with Limiting oxygen index of 31 %

Moisture absorption

23.0 °C

0.05 %

Show Supplier Material materials with Moisture absorption of 0.05 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.58 [-]

Show Supplier Material materials with Relative density of 1.58 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.3 %

Show Supplier Material materials with Water absorption of 0.3 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

12 GPa

Show Supplier Material materials with Elastic modulus of 12 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

ISO 178 | 2 mm/min

Flexural strain

23.0 °C

2 %

Show Supplier Material materials with Flexural strain of 2 %

ISO 178 | break, 2 mm/min

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ISO 178 | break, 2 mm/min

Hardness, Ball Indentation

23.0 °C

166 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 166 MPa

ISO 2039-1 | H358/30

Hardness, Rockwell R

23.0 °C

118 [-]

Show Supplier Material materials with Hardness, Rockwell R of 118 [-]

ISO 2039-2

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/2C | -30°C

Impact strength, Charpy unnotched

23.0 °C

30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m²

ISO 179/2C | 23°C

Impact strength, Izod notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A | notched 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

60 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m

ASTM D 256

Impact strength, Izod unnotched

23.0 °C

27 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 27 kJ/m²

ISO 180/1U | unnotched 80*10*4, -30°C

Impact strength, Izod unnotched, ASTM

23.0 °C

450 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 450 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

105 MPa

Show Supplier Material materials with Tensile strength of 105 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

2.1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.1E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

1.4E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.4E-4 1/K

ISO 11359-2 | 23°C to 150°C

Glow Wire Flammability Index

960 °C

Show Supplier Material materials with Glow Wire Flammability Index of 960 °C

Glow Wire Ignition Temperature

825 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C

IEC 60695-2-13 | 3.0 mm

Heat deflection temperature

180 - 215 °C

Show Supplier Material materials with Heat deflection temperature of 180 - 215 °C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

180 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 180 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

75 °C

Show Supplier Material materials with Relative temperature index, electrical of 75 °C

UL 746B

Relative temperature index, mechanical impact

75 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C

UL 746B

Relative temperature index, mechanical strength

75 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C

UL 746B

Vicat softening temperature

215 °C

Show Supplier Material materials with Vicat softening temperature of 215 °C

ISO 306 | Rate A/50

Flammability

UL Recognized, 94-5VA Flame Class Rating: ≥2mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 750°C IEC 60695-2-13 <br> Glow Wire Ignitability Temperature, 1.5 mm: 750°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 0.8 mm: 960°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100705592- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

2 V

Show Supplier Material materials with Comparative tracking index of 2 V

UL 746A | (UL) {PLC}

Dielectric constant, 1MHz

23.0 °C

3.6 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 3.6 [-]

IEC 60250

Dielectric strength

23.0 °C

35 kV/mm

Show Supplier Material materials with Dielectric strength of 35 kV/mm

IEC 60243-1 | in oil, 0.8 mm

Dissipation factor, 1MHz

23.0 °C

0.01 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-]

IEC 60250

High Amp Arc Ignition

23.0 °C

0.8 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.8 mm

≥, UL 746A | PLC 0

Hot-Wire Ignition

23.0 °C

0.8 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.8 mm

≥, UL 746A | PLC 0

Sheet resistivity, ROA

23.0 °C

1.00E+15 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω

>, IEC 60093

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11 g/10min

Show Supplier Material materials with Melt mass-flow rate of 11 g/10min

ISO 1133 | 250°C/5.0 kg

Melt viscosity

23.0 °C

155 Pa·s

Show Supplier Material materials with Melt viscosity of 155 Pa·s

ISO 11443 | 260°C, 1500 sec-1

Melt volume-flow rate

25 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 25 cm³/10min

ISO 1133 | MVR at 265°C/5.0 kg

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Wiring Devices, Electronic Components, Circuit Protection

Availability

Europe,Asia,Americas

Processing methods

Melt Temperature: 260 to 285.0°C
Front - Zone 3 Temperature: 260 to 280.0°C
Mold Temperature: 60 to 110.0°C
Maximum Moisture Content: 0.02%
Nozzle Temperature: 265 to 275.0°C
Rear - Zone 1 Temperature: 240 to 260.0°C
Hopper Temperature: 40 to 60.0°C
Drying Time: 4 to 6.0hrs
Middle - Zone 2 Temperature: 255 to 280.0°C
Drying Temperature: 110 to 120.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.