VALOX™ FR Resin ENH4530 - Asia

Want to keep this datasheet? Save it now in your required format

Description

VALOX ENH4530 is a 15% glass reinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.80mm flame rating. This is a good candidate for a variety of applications needing a sustainable FR PBT solution.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Medical Equipment General

Electrical Engineering

Electronics

Display Devices

Automotive

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.45 g/cm³ Show Supplier Material materials with Density of 1.45 g/cm³	ISO 1183
Limiting oxygen index	23.0 °C	31 % Show Supplier Material materials with Limiting oxygen index of 31 %
Moisture absorption	23.0 °C	0.07 % Show Supplier Material materials with Moisture absorption of 0.07 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.45 [-] Show Supplier Material materials with Relative density of 1.45 [-]	ASTM D 792
Water absorption	23.0 °C	0.15 % Show Supplier Material materials with Water absorption of 0.15 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	7.5 GPa Show Supplier Material materials with Elastic modulus of 7.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	3 % Show Supplier Material materials with Elongation of 3 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	6.4 GPa Show Supplier Material materials with Flexural modulus of 6.4 GPa	ISO 178 \| 2 mm/min
Flexural strain	23.0 °C	3 % Show Supplier Material materials with Flexural strain of 3 %	ISO 178 \| break, 2 mm/min
Flexural strength	23.0 °C	130 MPa Show Supplier Material materials with Flexural strength of 130 MPa	ISO 178 \| break, 2 mm/min
Hardness, Ball Indentation	23.0 °C	128 MPa Show Supplier Material materials with Hardness, Ball Indentation of 128 MPa	ISO 2039-1 \| H358/30
Hardness, Rockwell R	23.0 °C	98 [-] Show Supplier Material materials with Hardness, Rockwell R of 98 [-]	ISO 2039-2
Impact strength, Charpy notched	23.0 °C	6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m²	ISO 179/2C \| -30°C
Impact strength, Charpy unnotched	23.0 °C	25 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 25 kJ/m²	ISO 179/2C \| -30°C
Impact strength, Izod notched	23.0 °C	6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²	ISO 180/1A \| 80104, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	50 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 50 J/m	ASTM D 256 \| notched, -30°C
Impact strength, Izod unnotched	23.0 °C	23 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 23 kJ/m²	ISO 180/1U \| unnotched 80104, -30°C
Impact strength, Izod unnotched, ASTM	23.0 °C	400 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 400 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	80 MPa Show Supplier Material materials with Tensile strength of 80 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Ball Pressure Test		nan	IEC 60695-10-2 \| 125°C +/- 2°C
Coefficient of thermal expansion	23.0 °C	2.85E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.85E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		200 - 220 °C Show Supplier Material materials with Heat deflection temperature of 200 - 220 °C
Heat deflection temperature, 0.45 MPa		220 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 220 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		205 °C Show Supplier Material materials with Vicat softening temperature of 205 °C	ISO 306 \| Rate B/120

Electrical

Property	Temperature	Value	Comment
Dielectric constant, 1MHz	23.0 °C	3.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.7 [-]	IEC 60250
Dielectric strength	23.0 °C	21 kV/mm Show Supplier Material materials with Dielectric strength of 21 kV/mm	IEC 60243-1 \| in oil, 1.6 mm
Dissipation factor, 1MHz	23.0 °C	0.15 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.15 [-]	IEC 60250
Sheet resistivity, ROA	23.0 °C	1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω	>, IEC 60093
Volume resistivity	23.0 °C	1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm	IEC 60093

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		24 g/10min Show Supplier Material materials with Melt mass-flow rate of 24 g/10min	ASTM D 1238 \| 265°C/5.0 kgf
Melt viscosity	23.0 °C	150 Pa·s Show Supplier Material materials with Melt viscosity of 150 Pa·s	ISO 11443 \| 260°C, 1500 sec-1
Melt volume-flow rate		18 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 18 cm³/10min	ISO 1133 \| MVR at 265°C/5.0 kg
Shrinkage	23.0 °C	0.3 % Show Supplier Material materials with Shrinkage of 0.3 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Coil bobbin, Electronic Components, Enclosures, Heavy Vehicles, Lab Ware and Clinical Diagnostics, EV Infrastructure, Displays, Wireless Communications, Personal Computing, Respiratory
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 110 to 120.0°C Drying Time: 2 to 4.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 245 to 260.0°C Nozzle Temperature: 230 to 255.0°C Front - Zone 3 Temperature: 240 to 260.0°C Middle - Zone 2 Temperature: 235 to 250.0°C Rear - Zone 1 Temperature: 230 to 240.0°C Hopper Temperature: 40 to 60.0°C Mold Temperature: 40 to 100.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.