CYCOLOY™ FR Resin CX7510 - Americas

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CX7510 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable, high flow, high heat resistant, non chlorinated/brominated flame retardant grade. It has a UL94 V0@1.5mm and 5VB@1.5mm flame rating. This grade has improved chemical resistance compared to standard PC/ABS blends and is a good candidate for thin wall applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.18 g/cm³ Show Supplier Material materials with Density of 1.18 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.18 [-] Show Supplier Material materials with Relative density of 1.18 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.11 % Show Supplier Material materials with Water absorption of 0.11 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	4.5 % Show Supplier Material materials with Elongation of 4.5 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	99 MPa Show Supplier Material materials with Flexural strength of 99 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Izod notched	23.0 °C	640 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 640 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	640 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 640 J/m	ASTM D 256 \| notched, 23°C
Instrumented Impact, Total Energy	23.0 °C	65 J Show Supplier Material materials with Instrumented Impact, Total Energy of 65 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	48 MPa Show Supplier Material materials with Tensile strength of 48 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.2E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		95 °C Show Supplier Material materials with Heat deflection temperature of 95 °C
Heat deflection temperature, 1.80 MPa		95 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 95 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		115 °C Show Supplier Material materials with Vicat softening temperature of 115 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		16 g/10min Show Supplier Material materials with Melt mass-flow rate of 16 g/10min	ASTM D 1238 \| 260°C/2.16 kgf
Melt volume-flow rate		41 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 41 cm³/10min	ISO 1133 \| MVR at 260°C/5.0 kg
Shrinkage	23.0 °C	0.56 % Show Supplier Material materials with Shrinkage of 0.56 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Displays
Availability	Asia
Processing methods	Vent Depth: 0.038 to 0.076mm Front - Zone 3 Temperature: 265 to 300.0°C Drying Time (Cumulative): 8hrs Drying Temperature: 90 to 100.0°C Middle - Zone 2 Temperature: 260 to 300.0°C Maximum Moisture Content: 0.04% Rear - Zone 1 Temperature: 260 to 300.0°C Mold Temperature: 60 to 90.0°C Screw Speed: 40 to 70.0rpm Melt Temperature: 270 to 300.0°C Nozzle Temperature: 265 to 300.0°C Drying Time: 2 to 4.0hrs Shot to Cylinder Size: 40 to 80.0% Back Pressure: 0.3 to 0.7MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.