General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 4.8 % Show Supplier Material materials with Elongation of 4.8 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 98 MPa Show Supplier Material materials with Flexural strength of 98 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1A | 80*10*3, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 800 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 800 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 72 J Show Supplier Material materials with Instrumented Impact, Total Energy of 72 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 50 MPa Show Supplier Material materials with Tensile strength of 50 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 106 - 118 °C Show Supplier Material materials with Heat deflection temperature of 106 - 118 °C | ||
Heat deflection temperature, 0.45 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 118 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 106 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 106 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 127 °C Show Supplier Material materials with Vicat softening temperature of 127 °C | ISO 306 | Rate B/120 | |
Flammability | NBS Smoke Density, Flaming, Dmax: 225- ASTM E 662 <br> UL Recognized, 94-5VB Flame Class Rating: ≥2mm UL 94 <br> NBS Smoke Density, Flaming, Ds 1.5 min: 40- ASTM E 662 <br> UL Recognized, 94V-0 Flame Class Rating: ≥2mm UL 94 <br> NBS Smoke Density, Flaming, Ds 4 min: 150- ASTM E 662 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=600276- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15 g/10min Show Supplier Material materials with Melt mass-flow rate of 15 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Melt volume-flow rate | 12 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Enclosures, Data Transfer, Data Management, Security/Detection, Wiring Devices, Wireless Communications | |
Availability | Asia | |
Processing methods | Shot to Cylinder Size: 40 to 80.0% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |