Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.55 % Show Supplier Material materials with Moisture absorption of 0.55 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.42 [-] Show Supplier Material materials with Relative density of 1.42 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 1 % Show Supplier Material materials with Water absorption of 1 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.8 GPa Show Supplier Material materials with Elastic modulus of 6.8 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 5 % Show Supplier Material materials with Elongation of 5 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 6.5 GPa Show Supplier Material materials with Flexural modulus of 6.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 210 MPa Show Supplier Material materials with Flexural strength of 210 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 64 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 64 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 475 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 475 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 13 J Show Supplier Material materials with Instrumented Impact, Total Energy of 13 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 140 MPa Show Supplier Material materials with Tensile strength of 140 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 211 °C Show Supplier Material materials with Heat deflection temperature of 211 °C | ||||
Heat deflection temperature, 1.80 MPa | 211 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 211 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 170 °C Show Supplier Material materials with Relative temperature index, electrical of 170 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 170 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | |||
Vicat softening temperature | 218 °C Show Supplier Material materials with Vicat softening temperature of 218 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating: ≥1.9mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221093- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 3 mm Show Supplier Material materials with High Amp Arc Ignition of 3 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 8.4 g/10min Show Supplier Material materials with Melt mass-flow rate of 8.4 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Shrinkage | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices, Renal and Blood Handling, Medical Device, Lab Ware and Clinical Diagnostics | |
Availability | Europe,Asia,Americas | |
Processing methods | Shot to Cylinder Size: 40 to 60.0% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |