ULTEM™ Resin CRS5011 - Asia

Want to keep this datasheet? Save it now in your required format

Description

Transparent, Enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.89 GPa

Show Supplier Material materials with Elastic modulus of 2.89 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

60 %

Show Supplier Material materials with Elongation of 60 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.1 GPa

Show Supplier Material materials with Flexural modulus of 3.1 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

137 MPa

Show Supplier Material materials with Flexural strength of 137 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

58 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 58 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

99 MPa

Show Supplier Material materials with Tensile strength of 99 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

204 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 204 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

160 °C

Show Supplier Material materials with Relative temperature index, electrical of 160 °C

UL 746B

Relative temperature index, mechanical impact

155 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 155 °C

UL 746B

Relative temperature index, mechanical strength

160 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 160 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221115- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric constant, 60Hz

23.0 °C

3.2 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 3.2 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

17.9 kV/mm

Show Supplier Material materials with Dielectric strength of 17.9 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor, 50Hz

23.0 °C

2.1E-3 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 2.1E-3 [-]

ASTM D 150 | 50/60 Hz

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 0

High Volt Arc Track Rate

23.0 °C

3 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Fused Deposition Modeling (FDM), Enclosure/Housing/Cover, Electronic Components, Air Cabin Interiors, Aerospace, Aircraft Seating, Battery Cell, Data Transfer, Document Handling, Wireless Communications

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Enhanced Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant, Transparent

Processing methods

Shot to Cylinder Size: 40 to 60.0%
Back Pressure: 0.3 to 0.7MPa
Front - Zone 3 Temperature: 365 to 390.0°C
Drying Time: 4 to 6.0hrs
Nozzle Temperature: 360 to 380.0°C
Screw Speed: 40 to 70.0rpm
Mold Temperature: 135 to 165.0°C
Maximum Moisture Content: 0.02%
Drying Temperature: 150°C
Middle - Zone 2 Temperature: 355 to 375.0°C
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 365 to 390.0°C
Drying Time (Cumulative): 24hrs
Rear - Zone 1 Temperature: 345 to 365.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.