ULTEM™ Resin CRS5001 - Americas

Want to keep this datasheet? Save it now in your required format

Description

Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Water absorption

23.0 °C

0.16 %

Show Supplier Material materials with Water absorption of 0.16 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.89 GPa

Show Supplier Material materials with Elastic modulus of 2.89 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

60 %

Show Supplier Material materials with Elongation of 60 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.1 GPa

Show Supplier Material materials with Flexural modulus of 3.1 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

137 MPa

Show Supplier Material materials with Flexural strength of 137 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

64 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 64 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

99 MPa

Show Supplier Material materials with Tensile strength of 99 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

207 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 207 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

160 °C

Show Supplier Material materials with Relative temperature index, electrical of 160 °C

UL 746B

Relative temperature index, mechanical impact

160 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 160 °C

UL 746B

Relative temperature index, mechanical strength

160 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 160 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221114- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

17.9 kV/mm

Show Supplier Material materials with Dielectric strength of 17.9 kV/mm

ASTM D 149 | in oil, 3.2 mm

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 0

High Volt Arc Track Rate

23.0 °C

3 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Sheet resistivity, ROA

23.0 °C

5.80E+16 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 5.80E+16 Ω

ASTM D 257

Volume resistivity

23.0 °C

1.10E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.10E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Medical Device, LED Lighting, Meter Water, Photovoltaic Components, Semiconductor, Wireless Communications, Audio, Aerospace, Air Cabin Interiors, Electronic Components, Enclosure/Housing/Cover, Energy Management, Enclosures, Industrial Material Handling, Heavy Vehicles

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Enhanced Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant, Transparent

Processing methods

Shot to Cylinder Size: 40 to 60.0%
Drying Time (Cumulative): 24hrs
Melt Temperature: 365 to 390.0°C
Vent Depth: 0.025 to 0.076mm
Rear - Zone 1 Temperature: 345 to 365.0°C
Middle - Zone 2 Temperature: 355 to 375.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 40 to 70.0rpm
Drying Time: 4 to 6.0hrs
Nozzle Temperature: 360 to 380.0°C
Mold Temperature: 135 to 165.0°C
Front - Zone 3 Temperature: 365 to 390.0°C
Maximum Moisture Content: 0.02%
Drying Temperature: 150°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.