ULTEM™ Resin ATX200R - Europe

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 Listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.26 [-]

Show Supplier Material materials with Relative density of 1.26 [-]

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

70 %

Show Supplier Material materials with Elongation of 70 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.17 GPa

Show Supplier Material materials with Flexural modulus of 3.17 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

144 MPa

Show Supplier Material materials with Flexural strength of 144 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

53 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

53 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

96 MPa

Show Supplier Material materials with Tensile strength of 96 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

190 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 190 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

115 °C

Show Supplier Material materials with Relative temperature index, electrical of 115 °C

UL 746B

Relative temperature index, mechanical impact

115 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 115 °C

UL 746B

Relative temperature index, mechanical strength

115 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 115 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221073- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm

≥, UL 746A | PLC 4

Hot-Wire Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

26.5 g/10min

Show Supplier Material materials with Melt mass-flow rate of 26.5 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Circuit Protection, Data Transfer, City, Electronic Components, Enclosures, Forward Lighting, Motorcycle, Non-LED Lighting, Personal Computing

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant, High Impact Resistance, Good Mold Release

Processing methods

Shot to Cylinder Size: 40 to 60.0%
Back Pressure: 0.3 to 0.7MPa
Drying Time (Cumulative): 10hrs
Rear - Zone 1 Temperature: 340 to 360.0°C
Nozzle Temperature: 350 to 370.0°C
Front - Zone 3 Temperature: 350 to 370.0°C
Melt Temperature: 350 to 370.0°C
Mold Temperature: 135 to 165.0°C
Screw Speed: 40 to 70.0rpm
Drying Temperature: 135°C
Middle - Zone 2 Temperature: 345 to 365.0°C
Drying Time: 4 to 6.0hrs
Maximum Moisture Content: 0.02%
Vent Depth: 0.025 to 0.076mm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.