ULTEM™ Resin ATX200F - Americas

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend. ECO Conforming, UL94 V0 Listing. US FDA Food Contact compliant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

70 %

Show Supplier Material materials with Elongation of 70 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.17 GPa

Show Supplier Material materials with Flexural modulus of 3.17 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

144 MPa

Show Supplier Material materials with Flexural strength of 144 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

53 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

96 MPa

Show Supplier Material materials with Tensile strength of 96 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

190 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 190 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

115 °C

Show Supplier Material materials with Relative temperature index, electrical of 115 °C

UL 746B

Relative temperature index, mechanical impact

115 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 115 °C

UL 746B

Relative temperature index, mechanical strength

115 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 115 °C

UL 746B

Flammability

UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221073- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm

≥, UL 746A | PLC 4

Hot-Wire Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Surgical Devices, Small Appliance, Refrigerator, Microwave Oven, Medical Device, Non-LED Lighting, Motorcycle, Food Transportation, Lab Ware and Clinical Diagnostics, Electronic Components, Auto Aftermarket

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant, High Impact Resistance, Food Contact Acceptable

Processing methods

Vent Depth: 0.025 to 0.076mm
Melt Temperature: 350 to 370.0°C
Rear - Zone 1 Temperature: 340 to 360.0°C
Maximum Moisture Content: 0.02%
Mold Temperature: 135 to 165.0°C
Drying Temperature: 135°C
Screw Speed: 40 to 70.0rpm
Drying Time: 4 to 6.0hrs
Shot to Cylinder Size: 40 to 60.0%
Nozzle Temperature: 350 to 370.0°C
Back Pressure: 0.3 to 0.7MPa
Drying Time (Cumulative): 10hrs
Middle - Zone 2 Temperature: 345 to 365.0°C
Front - Zone 3 Temperature: 350 to 370.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.