ULTEM™ Resin ATX200 - Americas

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend. ECO Conforming, UL94 V0 Listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.26 [-]

Show Supplier Material materials with Relative density of 1.26 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

20 %

Show Supplier Material materials with Elongation of 20 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

3.1 GPa

Show Supplier Material materials with Flexural modulus of 3.1 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

125 MPa

Show Supplier Material materials with Flexural strength of 125 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | notched 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

53 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

2082 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2082 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

95 MPa

Show Supplier Material materials with Tensile strength of 95 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

180 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 180 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

115 °C

Show Supplier Material materials with Relative temperature index, electrical of 115 °C

UL 746B

Relative temperature index, mechanical impact

115 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 115 °C

UL 746B

Relative temperature index, mechanical strength

115 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 115 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100397331- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm

≥, UL 746A | PLC 4

Hot-Wire Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

24 g/10min

Show Supplier Material materials with Melt mass-flow rate of 24 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Data Management, Data Transfer, Air Cabin Interiors, Enclosures, Electronic Components, Individual Equiptment, Food Processor, Fog Lamp, Non-LED Lighting, Personal Computing, Microwave Oven, Power Manangement, Photo/Video Camera, Semiconductor, Wireless Communications

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant, High Impact Resistance

Processing methods

Front - Zone 3 Temperature: 340 to 360.0°C
Melt Temperature: 340 to 380.0°C
Nozzle Temperature: 340 to 360.0°C
Middle - Zone 2 Temperature: 330 to 350.0°C
Drying Temperature: 130 to 140.0°C
Hopper Temperature: 80 to 100.0°C
Mold Temperature: 125 to 140.0°C
Drying Time: 3 to 4.0hrs
Rear - Zone 1 Temperature: 320 to 340.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.