ULTEM™ Resin 2410R - Americas

Want to keep this datasheet? Save it now in your required format

Description

40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

54 %

Show Supplier Material materials with Limiting oxygen index of 54 %

Relative density

23.0 °C

1.61 [-]

Show Supplier Material materials with Relative density of 1.61 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.13 %

Show Supplier Material materials with Water absorption of 0.13 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.72 GPa

Show Supplier Material materials with Elastic modulus of 11.72 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

11.72 GPa

Show Supplier Material materials with Flexural modulus of 11.72 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

241 MPa

Show Supplier Material materials with Flexural strength of 241 MPa

ASTM D 790 | brk, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

112 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 112 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

112 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

427 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

179 MPa

Show Supplier Material materials with Tensile strength of 179 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.44E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

212 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 212 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Vicat softening temperature

234 °C

Show Supplier Material materials with Vicat softening temperature of 234 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221104- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

5 V

Show Supplier Material materials with Comparative tracking index of 5 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

24 kV/mm

Show Supplier Material materials with Dielectric strength of 24 kV/mm

ASTM D 149 | in oil, 1.6 mm

Dissipation factor, 1kHz

23.0 °C

2E-3 [-]

Show Supplier Material materials with Dissipation factor, 1kHz of 2E-3 [-]

ASTM D 150

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Volume resistivity

23.0 °C

1.50E+16 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.50E+16 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components, Document Handling, Data Transfer, Watch/Jewelry

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Good Mold Release

Processing methods

Drying Time (Cumulative): 24hrs
Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Mold Temperature: 135 to 165.0°C
Middle - Zone 2 Temperature: 340 to 400.0°C
Maximum Moisture Content: 0.02%
Back Pressure: 0.3 to 0.7MPa
Rear - Zone 1 Temperature: 330 to 400.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Melt Temperature: 350 to 400.0°C
Screw Speed: 40 to 70.0rpm
Nozzle Temperature: 345 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Shot to Cylinder Size: 40 to 60.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.