General
Property | Temperature | Value | Comment |
---|---|---|---|
Limiting oxygen index | 23.0 °C | 54 % Show Supplier Material materials with Limiting oxygen index of 54 % | |
Relative density | 23.0 °C | 1.61 [-] Show Supplier Material materials with Relative density of 1.61 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Water absorption of 0.13 % | ASTM D 570 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11.7 GPa Show Supplier Material materials with Elastic modulus of 11.7 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 11.7 GPa Show Supplier Material materials with Flexural modulus of 11.7 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 241 MPa Show Supplier Material materials with Flexural strength of 241 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 112 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 112 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 112 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 427 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 179 MPa Show Supplier Material materials with Tensile strength of 179 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.44E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Heat deflection temperature | 212 - 215 °C Show Supplier Material materials with Heat deflection temperature of 212 - 215 °C | ||||
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 212 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 212 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 170 °C Show Supplier Material materials with Relative temperature index, electrical of 170 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 170 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | |||
Vicat softening temperature | 234 °C Show Supplier Material materials with Vicat softening temperature of 234 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236986- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 5 V Show Supplier Material materials with Comparative tracking index of 5 V | UL 746A | (UL) {PLC} |
Dielectric strength | 23.0 °C | 24 kV/mm Show Supplier Material materials with Dielectric strength of 24 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Dissipation factor, 1kHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 2E-3 [-] | ASTM D 150 |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
Volume resistivity | 23.0 °C | 1.50E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.50E+16 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Document Handling, Data Transfer, Watch/Jewelry | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |