ULTEM™ Resin 2410R - Europe

Want to keep this datasheet? Save it now in your required format

Description

40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

48 %

Show Supplier Material materials with Limiting oxygen index of 48 %

Relative density

23.0 °C

1.61 [-]

Show Supplier Material materials with Relative density of 1.61 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.8 %

Show Supplier Material materials with Water absorption of 0.8 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.5 GPa

Show Supplier Material materials with Elastic modulus of 11.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

240 MPa

Show Supplier Material materials with Flexural strength of 240 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

112 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 112 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

112 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

427 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

180 MPa

Show Supplier Material materials with Tensile strength of 180 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

105 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Vicat softening temperature

230 °C

Show Supplier Material materials with Vicat softening temperature of 230 °C

ISO 306 | Rate A/50

Flammability

UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221104- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

16 kV/mm

Show Supplier Material materials with Dielectric strength of 16 kV/mm

IEC 60243-1 | in oil, 3.2 mm,

Dissipation factor, 1kHz

23.0 °C

2E-3 [-]

Show Supplier Material materials with Dissipation factor, 1kHz of 2E-3 [-]

IEC 60250

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Electronic Components, Document Handling, Data Transfer, Watch/Jewelry

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Good Mold Release

Processing methods

Hopper Temperature: 80 to 100.0°C
Melt Temperature: 370 to 410.0°C
Maximum Moisture Content: 0.02%
Nozzle Temperature: 370 to 410.0°C
Drying Temperature: 150°C
Middle - Zone 2 Temperature: 370 to 410.0°C
Drying Time: 4 to 6.0hrs
Front - Zone 3 Temperature: 380 to 420.0°C
Rear - Zone 1 Temperature: 350 to 390.0°C
Mold Temperature: 140 to 180.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.