ULTEM™ Resin 2410 - Europe

Want to keep this datasheet? Save it now in your required format

Description

40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

48 %

Show Supplier Material materials with Limiting oxygen index of 48 %

Water absorption

23.0 °C

0.8 %

Show Supplier Material materials with Water absorption of 0.8 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.5 GPa

Show Supplier Material materials with Elastic modulus of 11.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

240 MPa

Show Supplier Material materials with Flexural strength of 240 MPa

ISO 178 | break, 2 mm/min

Tensile strength

23.0 °C

180 MPa

Show Supplier Material materials with Tensile strength of 180 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Vicat softening temperature

225 °C

Show Supplier Material materials with Vicat softening temperature of 225 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221104- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

5 V

Show Supplier Material materials with Comparative tracking index of 5 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

26 kV/mm

Show Supplier Material materials with Dielectric strength of 26 kV/mm

IEC 60243-1 | in oil, 1.6 mm

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093 |

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Air Cabin Interiors, Electronic Components

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Mold Temperature: 140 to 180.0°C
Hopper Temperature: 80 to 100.0°C
Maximum Moisture Content: 0.02%
Drying Temperature: 150°C
Rear - Zone 1 Temperature: 350 to 390.0°C
Melt Temperature: 370 to 410.0°C
Front - Zone 3 Temperature: 380 to 420.0°C
Middle - Zone 2 Temperature: 370 to 410.0°C
Drying Time: 4 to 6.0hrs
Nozzle Temperature: 370 to 410.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.