ULTEM™ Resin 2400F - Europe

Want to keep this datasheet? Save it now in your required format

Description

40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2400.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.61 g/cm³

Show Supplier Material materials with Density of 1.61 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

48 %

Show Supplier Material materials with Limiting oxygen index of 48 %

Moisture absorption

23.0 °C

0.4 %

Show Supplier Material materials with Moisture absorption of 0.4 %

ISO 62 | (23°C / 50% RH)

Water absorption

23.0 °C

0.8 %

Show Supplier Material materials with Water absorption of 0.8 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.5 GPa

Show Supplier Material materials with Elastic modulus of 11.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

240 MPa

Show Supplier Material materials with Flexural strength of 240 MPa

ISO 178 | break, 2 mm/min

Hardness, Ball Indentation

23.0 °C

170 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 170 MPa

ISO 2039-1 | H358/30

Impact strength, Charpy unnotched

23.0 °C

40 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m²

ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod unnotched

23.0 °C

35 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 35 kJ/m²

ISO 180/1U | unnotched 80*10*4, -30°C

Taber Abrasion

23.0 °C

20 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 20 mg/1000cy

SABIC method | CS-17, 1 kg

Tensile strength

23.0 °C

180 MPa

Show Supplier Material materials with Tensile strength of 180 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

1.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

4.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Thermal conductivity

23.0 °C

0.33 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.33 W/(m·K)

ISO 8302

Vicat softening temperature

225 °C

Show Supplier Material materials with Vicat softening temperature of 225 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 875°C IEC 60695-2-13 <br> Glow Wire Ignitability Temperature, 1.0 mm: 850°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221103- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

5 V

Show Supplier Material materials with Comparative tracking index of 5 V

UL 746A | (UL) {PLC}

Dielectric constant, 1MHz

23.0 °C

3.1 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 3.1 [-]

IEC 60250

Dielectric constant, 60Hz

23.0 °C

3.5 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 3.5 [-]

IEC 60250 | 50/60 Hz

Dielectric strength

23.0 °C

26 kV/mm

Show Supplier Material materials with Dielectric strength of 26 kV/mm

IEC 60243-1 | in oil, 1.6 mm

Dissipation factor, 1MHz

23.0 °C

1.9E-3 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 1.9E-3 [-]

IEC 60250

Dissipation factor, 50Hz

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 2.5E-3 [-]

IEC 60250 | 50/60 Hz

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Sheet resistivity, ROA

23.0 °C

1.00E+15 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω

>, IEC 60093

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

5 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Coffee Maker/Espresso Machine, Individual Equiptment, Small Appliance

Availability

Europe

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Food Contact Acceptable

Processing methods

Hopper Temperature: 80 to 100.0°C
Drying Temperature: 150°C
Rear - Zone 1 Temperature: 350 to 390.0°C
Melt Temperature: 370 to 410.0°C
Nozzle Temperature: 370 to 410.0°C
Drying Time: 4 to 6.0hrs
Mold Temperature: 140 to 180.0°C
Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 380 to 420.0°C
Middle - Zone 2 Temperature: 370 to 410.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.