ULTEM™ Resin 2400 - Americas

Want to keep this datasheet? Save it now in your required format

Description

40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. WRAS certification in recognized colors.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

54 %

Show Supplier Material materials with Limiting oxygen index of 54 %

Water absorption

23.0 °C

0.13 %

Show Supplier Material materials with Water absorption of 0.13 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.72 GPa

Show Supplier Material materials with Elastic modulus of 11.72 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

11.72 GPa

Show Supplier Material materials with Flexural modulus of 11.72 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

241 MPa

Show Supplier Material materials with Flexural strength of 241 MPa

ASTM D 790 | brk, 2.6 mm/min, 100 mm span

Tensile strength

23.0 °C

179 MPa

Show Supplier Material materials with Tensile strength of 179 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.44E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

212 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 212 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

105 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Vicat softening temperature

234 °C

Show Supplier Material materials with Vicat softening temperature of 234 °C

ASTM D 1525 | Rate B/50

Flammability

NBS Smoke Density, Flaming, Ds 4 min: 1- ASTM E 662 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236985- - <br> Glow Wire Ignitability Temperature, 1.5 mm: 875°C IEC 60695-2-13 <br> Glow Wire Ignitability Temperature, 1.0 mm: 850°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

5 V

Show Supplier Material materials with Comparative tracking index of 5 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

24 kV/mm

Show Supplier Material materials with Dielectric strength of 24 kV/mm

ASTM D 149 | in oil, 1.6 mm

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Volume resistivity

23.0 °C

1.50E+16 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.50E+16 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wiring Devices, Wireless Communications, Swimming Pool/Spa, Structure, Oil/Gas, Medical Device, Monitoring and Imaging, Meter Gas, Photo/Video Camera, EV Infrastructure, Enclosures, Electronic Components, Air Cabin Interiors, Aircraft Seating, Circuit Protection, Data Management, Data Transfer, Document Handling, Defense Vehicles

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Screw Speed: 40 to 70.0rpm
Mold Temperature: 135 to 165.0°C
Vent Depth: 0.025 to 0.076mm
Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Maximum Moisture Content: 0.02%
Rear - Zone 1 Temperature: 330 to 400.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Drying Time (Cumulative): 24hrs
Middle - Zone 2 Temperature: 340 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%
Nozzle Temperature: 345 to 400.0°C
Melt Temperature: 350 to 400.0°C
Back Pressure: 0.3 to 0.7MPa

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.