Properties
General
| Property | Temperature | Value |
|---|---|---|
Limiting oxygen index | 23.0 °C | 50 % Show Supplier Material materials with Limiting oxygen index of 50 % |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 6.9 GPa Show Supplier Material materials with Elastic modulus of 6.9 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 4 % Show Supplier Material materials with Elongation of 4 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 6.9 GPa Show Supplier Material materials with Flexural modulus of 6.9 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 227 MPa Show Supplier Material materials with Flexural strength of 227 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Tensile strength | 23.0 °C | 139 MPa Show Supplier Material materials with Tensile strength of 139 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature | 210 - 211 °C Show Supplier Material materials with Heat deflection temperature of 210 - 211 °C | ||
Heat deflection temperature, 0.45 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 211 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 211 °C | ASTM D 648 | 6.4 mm, unannealed | |
Relative temperature index, electrical | 170 °C Show Supplier Material materials with Relative temperature index, electrical of 170 °C | UL 746B | |
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |
Relative temperature index, mechanical strength | 170 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | |
Vicat softening temperature | 225 °C Show Supplier Material materials with Vicat softening temperature of 225 °C | ASTM D 1525 | Rate B/50 | |
Flammability | UL Recognized, 94-5VA Flame Class Rating: ≥1.9mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> NBS Smoke Density, Flaming, Ds 4 min: 1.3- ASTM E 662 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221093- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=502535- - | ||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 3 mm Show Supplier Material materials with High Amp Arc Ignition of 3 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Meter Gas, Oil/Gas, Pharmaceutical Packaging & Drug Delivery, Wireless Communications, Wiring Devices, Data Transfer, Data Management, Document Handling, Aerospace, Circuit Protection, Auto Aftermarket, Energy Management, Enclosure/Housing/Cover, Enclosures, Electronic Components, Wire & cable | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Back Pressure: 0.3 to 0.7MPa | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |