ULTEM™ Resin 2110R - Europe

Want to keep this datasheet? Save it now in your required format

Description

10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.5 GPa

Show Supplier Material materials with Elastic modulus of 4.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

4 %

Show Supplier Material materials with Elongation of 4 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

4.5 GPa

Show Supplier Material materials with Flexural modulus of 4.5 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

185 MPa

Show Supplier Material materials with Flexural strength of 185 MPa

ISO 178 | break, 2 mm/min

Tensile strength

23.0 °C

115 MPa

Show Supplier Material materials with Tensile strength of 115 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

205 °C

Show Supplier Material materials with Heat deflection temperature of 205 °C

Heat deflection temperature, 1.80 MPa

205 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥1.9mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=502535- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=100732301- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

3 mm

Show Supplier Material materials with High Amp Arc Ignition of 3 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

2 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 1

Technological properties

Property
Application areas

Personal Computing, Personal Care, Wireless Communications, Data Transfer, Data Management, Displays, Aircraft Seating, Building Accessory, Electronic Components, Enclosures

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Good Mold Release

Processing methods

Nozzle Temperature: 350 to 405.0°C
Front - Zone 3 Temperature: 360 to 415.0°C
Middle - Zone 2 Temperature: 350 to 405.0°C
Melt Temperature: 370 to 410.0°C
Rear - Zone 1 Temperature: 340 to 395.0°C
Hopper Temperature: 80 to 120.0°C
Drying Time: 4 to 6.0hrs
Maximum Moisture Content: 0.02%
Drying Temperature: 150°C
Mold Temperature: 140 to 180.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.