ULTEM™ Resin 1010R - Asia

Want to keep this datasheet? Save it now in your required format

Description

Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

44 %

Show Supplier Material materials with Limiting oxygen index of 44 %

Water absorption

23.0 °C

0.25 %

Show Supplier Material materials with Water absorption of 0.25 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.58 GPa

Show Supplier Material materials with Elastic modulus of 3.58 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ASTM D 638 | yld, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.51 GPa

Show Supplier Material materials with Flexural modulus of 3.51 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

32 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 32 kJ/m²

ASTM D 256 | notched, 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.58E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature, 0.45 MPa

207 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 207 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

198 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Thermal conductivity

23.0 °C

0.22 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K)

ASTM C177

Vicat softening temperature

218 °C

Show Supplier Material materials with Vicat softening temperature of 218 °C

ASTM D 1525 | Rate B/50

Flammability

NBS Smoke Density, Flaming, Ds 4 min: 2- ASTM E 662 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥3mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101048269- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

28 kV/mm

Show Supplier Material materials with Dielectric strength of 28 kV/mm

ASTM D 149 | in oil, 1.6 mm

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

ASTM D 150 | 2450 MHz

High Amp Arc Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

2 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm

≥, UL 746A | PLC 2

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wireless Communications, Swimming Pool/Spa, Pharmaceutical Packaging & Drug Delivery, Surgical Devices, Renal and Blood Handling, Motorcycle, Personal Computing, Medical Device, Monitoring and Imaging, Ignition System, Lab Ware and Clinical Diagnostics, Forward Lighting, Electronic Components, Enclosures, Enclosure/Housing/Cover, Building Accessory, Auto Aftermarket, Aerospace, Air Cabin Interiors, Data Management, Data Transfer, Displays, Wire & cable

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Good Mold Release

Processing methods

Screw Speed: 40 to 70.0rpm
Rear - Zone 1 Temperature: 330 to 400.0°C
Middle - Zone 2 Temperature: 340 to 400.0°C
Melt Temperature: 350 to 400.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Maximum Moisture Content: 0.02%
Nozzle Temperature: 345 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%
Mold Temperature: 135 to 165.0°C
Drying Time: 4 to 6.0hrs
Drying Temperature: 150°C
Back Pressure: 0.3 to 0.7MPa
Drying Time (Cumulative): 24hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.