ULTEM™ Resin 1000F - Americas

Want to keep this datasheet? Save it now in your required format

Description

ULTEMTM 1000F resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217?C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS, US FDA and EU Food Contact compliant, with NSF 51 listing. ULTEMTM 1000F resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

47 %

Show Supplier Material materials with Limiting oxygen index of 47 %

Water absorption

23.0 °C

0.25 %

Show Supplier Material materials with Water absorption of 0.25 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.58 GPa

Show Supplier Material materials with Elastic modulus of 3.58 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

60 %

Show Supplier Material materials with Elongation of 60 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.51 GPa

Show Supplier Material materials with Flexural modulus of 3.51 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

53 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m²

ASTM D 256 | notched, 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.58E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K

ASTM E 831 | -20°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

5.4E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.4E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature, 0.45 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

201 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 201 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Thermal conductivity

23.0 °C

0.22 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K)

ASTM C177

Vicat softening temperature

218 °C

Show Supplier Material materials with Vicat softening temperature of 218 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> NBS Smoke Density, Flaming, Ds 4 min: 0.7- ASTM E 662 <br> UL Recognized, 94-5VA Flame Class Rating: ≥3mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101048254- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

28 kV/mm

Show Supplier Material materials with Dielectric strength of 28 kV/mm

ASTM D 149 | in oil, 1.6 mm

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

ASTM D 150 | 2450 MHz

High Amp Arc Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

2 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

0.75 mm

Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm

≥, UL 746A | PLC 2

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wireless Communications, Tray, Surgical Tray, Oil/Gas, Personal Care, Medical Device, Laundry Dryer, Monitoring and Imaging, Power Manangement, Refrigerator, Surgical Devices, Semiconductor, Respiratory, Commercial Storage/Cookware, Coffee Maker/Espresso Machine, Data Management, Displays, Airline Service, Building Accessory, Aerospace, Aircraft Seating, Air Cabin Interiors, Electronic Components, Enclosure/Housing/Cover, Electronic Material Handling, Food Processor

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant, Food Contact Acceptable

Processing methods

Nozzle Temperature: 345 to 400.0°C
Back Pressure: 0.3 to 0.7MPa
Front - Zone 3 Temperature: 345 to 400.0°C
Mold Temperature: 135 to 165.0°C
Shot to Cylinder Size: 40 to 60.0%
Screw Speed: 40 to 70.0rpm
Rear - Zone 1 Temperature: 330 to 400.0°C
Drying Time: 4 to 6.0hrs
Maximum Moisture Content: 0.02%
Middle - Zone 2 Temperature: 340 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 350 to 400.0°C
Drying Time (Cumulative): 24hrs
Drying Temperature: 150°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.