NORYL PPX™ Resin PPX7110 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 7110 resin is a non-reinforced alloy of polyphenylene ether (PPE) + Polypropylene (PP). This injection moldable grade exhibits high impact resistance and good heat resistance along with hydrolytic and dimensional stability. NORYL PPX7110 resin is an excellent candidate for applications requiring high impact, chemical resistance, and good heat performance.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.34 GPa

Show Supplier Material materials with Elastic modulus of 1.34 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

195 %

Show Supplier Material materials with Elongation of 195 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

1.55 GPa

Show Supplier Material materials with Flexural modulus of 1.55 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

51 MPa

Show Supplier Material materials with Flexural strength of 51 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

437 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 437 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

32 MPa

Show Supplier Material materials with Tensile strength of 32 MPa

ASTM D 638 | brk, Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

8.1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 8.1E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

1.12E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.12E-4 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

113 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 113 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

77 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 77 °C

ASTM D 648 | 3.2mm, unannealed

Vicat softening temperature

138 °C

Show Supplier Material materials with Vicat softening temperature of 138 °C

ASTM D 1525 | Rate B/50

Technological properties

Property
Application areas

Medical Device, Wiring Devices, Hot Water System, EV/HEV Battery, Document Handling

Availability

Europe,Asia,Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Low Warpage, High Impact Resistance

Processing methods

Nozzle Temperature: 260 to 290.0°C
Die Temperature: 265 to 270.0°C
Shot to Cylinder Size: 30 to 70.0%
Drying Time (Cumulative): 4hrs
Vent Depth: 0.038 to 0.051mm
Barrel - Zone 2 Temperature: 255 to 265.0°C
Maximum Moisture Content: 0.02%
Melt Temperature: 260 to 290.0°C
Drying Temperature: 60 to 65.0°C
Drying Time: 2 to 4.0hrs
Drying Temperature: 60 to 65.0°C
Rear - Zone 1 Temperature: 225 to 275.0°C
Back Pressure: 0.3 to 0.7MPa
Barrel - Zone 1 Temperature: 145 to 155.0°C
Drying Time: 2 to 4.0hrs
Barrel - Zone 4 Temperature: 270 to 280.0°C
Middle - Zone 2 Temperature: 240 to 280.0°C
Drying Time (Cumulative): 8hrs
Mold Temperature: 30 to 50.0°C
Adapter Temperature: 265 to 270.0°C
Melt Temperature: 270 to 280.0°C
Front - Zone 3 Temperature: 250 to 290.0°C
Screw Speed: 20 to 100.0rpm
Barrel - Zone 3 Temperature: 270 to 280.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.