NORYL PPX™ Resin PPX7110 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 7110 resin is a non-reinforced alloy of polyphenylene ether (PPE) + Polypropylene (PP). This injection moldable grade exhibits high impact resistance and good heat resistance along with hydrolytic and dimensional stability. NORYL PPX7110 resin is an excellent candidate for applications requiring high impact, chemical resistance, and good heat performance.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.5 GPa

Show Supplier Material materials with Elastic modulus of 1.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

195 %

Show Supplier Material materials with Elongation of 195 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

1.7 GPa

Show Supplier Material materials with Flexural modulus of 1.7 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

50 MPa

Show Supplier Material materials with Flexural strength of 50 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

9 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m²

ISO 180/1A | notched 80*10*4, -30°C

Tensile strength

23.0 °C

34 MPa

Show Supplier Material materials with Tensile strength of 34 MPa

ISO 527 | yield, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K

ISO 11359-2 | 23°C to 60°C

Coefficient of thermal expansion, transverse

23.0 °C

1.2E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K

ISO 11359-2 | 23°C to 60°C

Heat deflection temperature, 0.45 MPa

108 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 108 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

75 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 75 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

100 °C

Show Supplier Material materials with Vicat softening temperature of 100 °C

ISO 306 | Rate B/120

Technological properties

Property
Application areas

Medical Device, Wiring Devices, Hot Water System, EV/HEV Battery, Document Handling

Availability

Europe,Asia,Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Low Warpage, High Impact Resistance

Processing methods

Drying Time: 2 to 4.0hrs
Middle - Zone 2 Temperature: 240 to 285.0°C
Front - Zone 3 Temperature: 250 to 290.0°C
Drying Temperature: 60 to 65.0°C
Mold Temperature: 40 to 60.0°C
Hopper Temperature: 60 to 80.0°C
Nozzle Temperature: 260 to 290.0°C
Maximum Moisture Content: 0.02%
Rear - Zone 1 Temperature: 225 to 275.0°C
Melt Temperature: 260 to 290.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.