NORYL PPX™ Resin PPX640 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 640 resin is a 40% glass reinforced alloy of polyphenylene ether (PPE) + Polypropylene (PP). This injection moldable grade exhibits high stiffness along with temperature performance, impact resistance, hydrolytic stability, and dimensional stability. NORYL PPX640 resin is an excellent candidate for applications requiring a good chemical resistance and high stiffness.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

6.4 %

Show Supplier Material materials with Elongation of 6.4 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

8.3 GPa

Show Supplier Material materials with Flexural modulus of 8.3 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

150 MPa

Show Supplier Material materials with Flexural strength of 150 MPa

ASTM D 790 | brk, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

106 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 106 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

95 MPa

Show Supplier Material materials with Tensile strength of 95 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.08E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.08E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.3E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature

146 - 158 °C

Show Supplier Material materials with Heat deflection temperature of 146 - 158 °C

Heat deflection temperature, 0.45 MPa

158 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 158 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

146 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 146 °C

ASTM D 648 | 3.2mm, unannealed

Vicat softening temperature

163 °C

Show Supplier Material materials with Vicat softening temperature of 163 °C

ASTM D 1525 | Rate B/50

Technological properties

Property
Application areas

Water Treatment/Filtration, Hot Water System

Availability

Europe,Asia,Americas

Processing methods

Drying Time (Cumulative): 8hrs
Drying Time: 2 to 4.0hrs
Vent Depth: 0.051 to 0.076mm
Back Pressure: 0.3 to 0.7MPa
Shot to Cylinder Size: 30 to 70.0%
Mold Temperature: 40 to 65.0°C
Drying Temperature: 65 to 75.0°C
Rear - Zone 1 Temperature: 245 to 290.0°C
Screw Speed: 20 to 100.0rpm
Maximum Moisture Content: 0.02%
Melt Temperature: 260 to 305.0°C
Middle - Zone 2 Temperature: 250 to 290.0°C
Front - Zone 3 Temperature: 255 to 300.0°C
Nozzle Temperature: 260 to 305.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.