NORYL PPX™ Resin PPX640 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 640 resin is a 40% glass reinforced alloy of polyphenylene ether (PPE) + Polypropylene (PP). This injection moldable grade exhibits high stiffness along with temperature performance, impact resistance, hydrolytic stability, and dimensional stability. NORYL PPX640 resin is an excellent candidate for applications requiring a good chemical resistance and high stiffness.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2.2 %

Show Supplier Material materials with Elongation of 2.2 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

8.5 GPa

Show Supplier Material materials with Flexural modulus of 8.5 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

150 MPa

Show Supplier Material materials with Flexural strength of 150 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Tensile strength

23.0 °C

100 MPa

Show Supplier Material materials with Tensile strength of 100 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K

ISO 11359-2 | 23°C to 60°C

Coefficient of thermal expansion, transverse

23.0 °C

9.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9.5E-5 1/K

ISO 11359-2 | 23°C to 60°C

Heat deflection temperature

145 - 158 °C

Show Supplier Material materials with Heat deflection temperature of 145 - 158 °C

Heat deflection temperature, 0.45 MPa

158 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 158 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

145 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

138 °C

Show Supplier Material materials with Vicat softening temperature of 138 °C

ISO 306 | Rate B/50

Technological properties

Property
Application areas

Water Treatment/Filtration, Hot Water System

Availability

Europe,Asia,Americas

Processing methods

Maximum Moisture Content: 0.02%
Nozzle Temperature: 260 to 305.0°C
Hopper Temperature: 60 to 80.0°C
Front - Zone 3 Temperature: 255 to 300.0°C
Drying Time: 2 to 4.0hrs
Rear - Zone 1 Temperature: 245 to 290.0°C
Mold Temperature: 40 to 65.0°C
Melt Temperature: 260 to 305.0°C
Middle - Zone 2 Temperature: 250 to 290.0°C
Drying Temperature: 65 to 75.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.