NORYL™ Resin NH6010B - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NH6010B resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high performance, injection moldable and extrusion grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm. NORYL NH6010B resin features low smoke production upon burning, high heat resistance, very low specific gravity, and compliance to IEC. In addition, this material is heat stabilized and impact modified. It is an excellent candidate for conduit and trunking applications in transportation, building + construction, and electrical markets. *see NORYL LS6010 resin for FAR 25.853 requirements.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Energy

Electrical Engineering

Railway

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.11 g/cm³ Show Supplier Material materials with Density of 1.11 g/cm³	ISO 1183
Limiting oxygen index	23.0 °C	33 % Show Supplier Material materials with Limiting oxygen index of 33 %
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.11 [-] Show Supplier Material materials with Relative density of 1.11 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.2 % Show Supplier Material materials with Water absorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	8.3 % Show Supplier Material materials with Elongation of 8.3 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	100 MPa Show Supplier Material materials with Flexural strength of 100 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 14 kJ/m²	ISO 180/1A \| 80104, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	300 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 300 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	58 MPa Show Supplier Material materials with Tensile strength of 58 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		124 °C Show Supplier Material materials with Heat deflection temperature of 124 °C
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		143 °C Show Supplier Material materials with Vicat softening temperature of 143 °C	ISO 306 \| Rate B/50
Flammability	Ds_4min: 70- ISO 5659-2 <br> Lateral Flame Spread, CFE: 20kW/m² ISO 5658-2 <br> M1 Flame Class Rating: 2mm NF P 92501 <br> Glow Wire Ignitability Temperature, 1.0 mm: 775°C IEC 60695-2-13 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Toxicity (3 mm): 21.76- NF X70-100 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (3.2 mm): 30- ASTM E 662 <br> Heat Release, MAHRE: 33.6kW/m² ISO 5660-1 <br> Toxicity: 0- ISO 5659-2 <br> F1 Class Smoke and Toxicity Rating: 3mm NF F16-101 <br> NBS Smoke Density, Flaming, 20 min (3.2 mm): 120- ASTM E 662 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Ignitability Temperature, 1.5 mm: 775°C IEC 60695-2-13 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100050086- -

Electrical

Property	Temperature	Value	Comment
Dielectric constant, 1MHz	23.0 °C	2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-]	IEC 60250
Dielectric strength	23.0 °C	34.1 kV/mm Show Supplier Material materials with Dielectric strength of 34.1 kV/mm	IEC 60243-1 \| in oil, 3.2 mm,
Dissipation factor, 1MHz	23.0 °C	2.9E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2.9E-3 [-]	IEC 60250
Sheet resistivity, ROA	23.0 °C	1.25E+18 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.25E+18 Ω	IEC 60093
Volume resistivity	23.0 °C	7.62E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 7.62E+17 Ω·cm	IEC 60093 \|

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		5.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 5.6 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate		5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Exterior Rail Components, Fuel Cell, Rail, Wiring Devices, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Barrel - Zone 1 Temperature: 220 to 260.0°C Barrel - Zone 2 Temperature: 220 to 260.0°C Drying Temperature: 95 to 105.0°C Melt Temperature: 280 to 305.0°C Drying Time: 2 to 4.0hrs Front - Zone 3 Temperature: 295 to 305.0°C Calibrator Temperature: 30 to 60.0°C Drying Time (Cumulative): 12hrs Drying Temperature: 95 to 105.0°C Drying Temperature: 95 to 105.0°C Die Temperature: 220 to 260.0°C Die Temperature: 220 to 260.0°C Barrel - Zone 3 Temperature: 220 to 260.0°C Barrel - Zone 3 Temperature: 220 to 260.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Screw Speed: 40 to 80.0rpm Middle - Zone 2 Temperature: 290 to 300.0°C Water Bath Temperature: 30 to 50.0°C Maximum Moisture Content: 0.07% Maximum Moisture Content: 0.07% Shot to Cylinder Size: 30 to 70.0% Drying Time: 2 to 4.0hrs Melt Temperature: 220 to 260.0°C Drying Time (Cumulative): 12hrs Melt Temperature: 220 to 260.0°C Adapter Temperature: 220 to 260.0°C Roll Stack Temp - Top: 90 to 150.0°C Mold Temperature: 65 to 100.0°C Hopper Temperature: 80 to 120.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Roll Stack Temp - Bottom: 90 to 150.0°C Barrel - Zone 2 Temperature: 220 to 260.0°C Roll Stack Temp - Middle: 90 to 150.0°C Drying Time: 2 to 4.0hrs Nozzle Temperature: 295 to 305.0°C Adapter Temperature: 220 to 260.0°C Rear - Zone 1 Temperature: 280 to 295.0°C Drying Time (Cumulative): 12hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.