NORYL™ Resin GFN30 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ GFN30 resin is a 30% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This general-purpose injection moldable grade exhibits very low moisture absorption, high strength, hydrolytic stability, Low warpage, low specific gravity, and dimensional stability. NORYL GFN30 carries a UL746C outdoor suitability rating of F2 and is an excellent candidate for a variety of indoor and outdoor applications including construction, electrical components + displays, lawn and garden equipment. *See NORYL GFN30F resin for FDA food compliant / NSF version.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Moisture absorption

23.0 °C

0.04 %

Show Supplier Material materials with Moisture absorption of 0.04 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.31 [-]

Show Supplier Material materials with Relative density of 1.31 [-]

ASTM D 792

Water absorption

23.0 °C

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

8.2 GPa

Show Supplier Material materials with Elastic modulus of 8.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

6.8 GPa

Show Supplier Material materials with Flexural modulus of 6.8 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

160 MPa

Show Supplier Material materials with Flexural strength of 160 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

120 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 120 J/m

ASTM D 256 | notched, -30°C

Impact strength, Izod unnotched

23.0 °C

30 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m²

ISO 180/1U | 80*10*4, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

590 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 590 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

20 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 20 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.3E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

139 - 147 °C

Show Supplier Material materials with Heat deflection temperature of 139 - 147 °C

Heat deflection temperature, 0.45 MPa

147 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 147 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

139 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 139 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

90 °C

Show Supplier Material materials with Relative temperature index, electrical of 90 °C

UL 746B

Relative temperature index, mechanical impact

90 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 90 °C

UL 746B

Relative temperature index, mechanical strength

90 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 90 °C

UL 746B

Vicat softening temperature

149 °C

Show Supplier Material materials with Vicat softening temperature of 149 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UV-light, water exposure/immersion: F2- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228546- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237022- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

3 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

3.2 g/10min

Show Supplier Material materials with Melt mass-flow rate of 3.2 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

2 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 2 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Air Conditioning

Availability

Asia

Features

Hydrolytic Stability, Low Warpage, Structural

Processing methods

Drying Temperature: 110 to 120.0°C
Drying Time: 3 to 4.0hrs
Drying Time (Cumulative): 8hrs
Maximum Moisture Content: 0.02%
Melt Temperature: 300 to 325.0°C
Nozzle Temperature: 300 to 325.0°C
Front - Zone 3 Temperature: 290 to 325.0°C
Middle - Zone 2 Temperature: 275 to 320.0°C
Rear - Zone 1 Temperature: 265 to 315.0°C
Mold Temperature: 80 to 110.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 20 to 100.0rpm
Shot to Cylinder Size: 30 to 70.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.