NORYL™ Resin GFN1 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ GFN1 resin is a 10% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This general-purpose injection moldable grade exhibits very low moisture absorption, high strength, hydrolytic stability, Low warpage, low specific gravity, and dimensional stability. NORYL GFN1 carries a UL746C outdoor suitability rating of F1 and is an excellent candidate for a variety of indoor and outdoor applications including construction, electrical components + displays, lawn and garden equipment. *See NORYL GFN1F resin for FDA food compliant / NSF version.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Water absorption

23.0 °C

0.12 %

Show Supplier Material materials with Water absorption of 0.12 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.9 GPa

Show Supplier Material materials with Elastic modulus of 3.9 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ISO 527 | break

Flexural modulus

23.0 °C

4.2 GPa

Show Supplier Material materials with Flexural modulus of 4.2 GPa

ISO 178

Flexural strength

23.0 °C

115 MPa

Show Supplier Material materials with Flexural strength of 115 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod unnotched

23.0 °C

30 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m²

ISO 180/1U | unnotched 80*10*4, -30°C

Tensile strength

23.0 °C

60 MPa

Show Supplier Material materials with Tensile strength of 60 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

3.8E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 3.8E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K

ISO 11359-2 | 23°C to 80°C

Heat deflection temperature

124 - 132 °C

Show Supplier Material materials with Heat deflection temperature of 124 - 132 °C

Heat deflection temperature, 0.45 MPa

132 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 132 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

124 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

138 °C

Show Supplier Material materials with Vicat softening temperature of 138 °C

ISO 306 | Rate B/50

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228544- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237019- -

Electrical

PropertyTemperatureValueComment

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 0

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

8 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Document Handling, Coffee Maker/Espresso Machine, Data Transfer, Air Conditioning, Air Filtration, Building Accessory, Circuit Protection, Enclosure/Housing/Cover, Energy Management, Enclosures, Electronic Components, Fixture Bath/Shower, Furnace/Heater, Hot Water System, Heavy Vehicles, Individual Equiptment, Lab Ware and Clinical Diagnostics, Swimming Pool/Spa, Water Treatment/Filtration, Wiring Devices, Wireless Communications, Medical Device, Meter Gas, Personal Computing, Recreational Vehicle, Pump, Pipe/Fitting, Plumbing, Security/Detection, Respiratory, Sanitary, Small Appliance, Irrigation

Availability

Europe,Asia,Americas

Processing methods

Screw Speed: 20 to 100.0rpm
Front - Zone 3 Temperature: 280 to 315.0°C
Back Pressure: 0.3 to 0.7MPa
Middle - Zone 2 Temperature: 270 to 310.0°C
Drying Temperature: 105 to 110.0°C
Drying Time (Cumulative): 8hrs
Mold Temperature: 75 to 105.0°C
Melt Temperature: 295 to 315.0°C
Rear - Zone 1 Temperature: 260 to 305.0°C
Drying Time: 3 to 4.0hrs
Nozzle Temperature: 295 to 315.0°C
Maximum Moisture Content: 0.02%
Shot to Cylinder Size: 30 to 70.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.