Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Water absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 4.4 GPa Show Supplier Material materials with Elastic modulus of 4.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 3.7 GPa Show Supplier Material materials with Flexural modulus of 3.7 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 122 MPa Show Supplier Material materials with Flexural strength of 122 MPa | ISO 178 |
Impact strength, Izod unnotched | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 20 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Tensile strength | 23.0 °C | 45 MPa Show Supplier Material materials with Tensile strength of 45 MPa | ISO 527 | break, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 129 - 130 °C Show Supplier Material materials with Heat deflection temperature of 129 - 130 °C | ||||
Heat deflection temperature, 0.45 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 130 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 129 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Vicat softening temperature | 125 °C Show Supplier Material materials with Vicat softening temperature of 125 °C | ISO 306 | Rate B/50 | |||
Flammability | Glow Wire Flammability Index 750°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236754- - | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 4 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 4 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.55 % Show Supplier Material materials with Shrinkage of 0.55 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Document Handling, Coffee Maker/Espresso Machine, Data Transfer, Air Conditioning, Air Filtration, Building Accessory, Circuit Protection, Enclosure/Housing/Cover, Energy Management, Enclosures, Electronic Components, Fixture Bath/Shower, Furnace/Heater, Hot Water System, Heavy Vehicles, Individual Equiptment, Lab Ware and Clinical Diagnostics, Swimming Pool/Spa, Water Treatment/Filtration, Wiring Devices, Wireless Communications, Medical Device, Meter Gas, Personal Computing, Recreational Vehicle, Pump, Pipe/Fitting, Plumbing, Security/Detection, Respiratory, Sanitary, Small Appliance, Irrigation | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Mold Temperature: 80 to 120.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |