NORYL™ Resin EM6101 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ EM6101 is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade has improved flow characteristics and overall processing economy with a heat deflection temperature (HDT) of 123c and good property retention over a wide temperature range. NORYL EM6101 resin is an excellent candidate for automotive interior applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.05 [-]

Show Supplier Material materials with Relative density of 1.05 [-]

ASTM D 792

Water absorption

23.0 °C

0.2 %

Show Supplier Material materials with Water absorption of 0.2 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

2.3 GPa

Show Supplier Material materials with Flexural modulus of 2.3 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

81 MPa

Show Supplier Material materials with Flexural strength of 81 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

320 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 320 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

160 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 160 J/m

ASTM D 256 | -40°C

Instrumented Impact, at Peak

23.0 °C

25 J

Show Supplier Material materials with Instrumented Impact, at Peak of 25 J

ASTM D 3763 | -30

Tensile strength

23.0 °C

53 MPa

Show Supplier Material materials with Tensile strength of 53 MPa

ASTM D 638 | yld, Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

9.36E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9.36E-5 1/K

ASTM E 831 | 0°C to 100°C

Heat deflection temperature

121 - 123 °C

Show Supplier Material materials with Heat deflection temperature of 121 - 123 °C

Heat deflection temperature, 0.45 MPa

123 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 123 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

121 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C

ASTM D 648 | 6.4 mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components

Availability

Americas

Processing methods

Drying Time: 3 to 4.0hrs
Melt Temperature: 265 to 295.0°C
Mold Temperature: 65 to 95.0°C
Vent Depth: 0.038 to 0.051mm
Shot to Cylinder Size: 30 to 70.0%
Maximum Moisture Content: 0.02%
Drying Time (Cumulative): 8hrs
Front - Zone 3 Temperature: 255 to 295.0°C
Nozzle Temperature: 265 to 295.0°C
Rear - Zone 1 Temperature: 230 to 280.0°C
Screw Speed: 20 to 100.0rpm
Middle - Zone 2 Temperature: 245 to 290.0°C
Drying Temperature: 95 to 105.0°C
Back Pressure: 0.3 to 0.7MPa

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.