General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.11 g/cm³ Show Supplier Material materials with Density of 1.11 g/cm³ | ISO 1183 |
Relative density | 23.0 °C | 1.11 [-] Show Supplier Material materials with Relative density of 1.11 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 0.07 % Show Supplier Material materials with Water absorption of 0.07 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Elastic modulus of 2.7 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 105 MPa Show Supplier Material materials with Flexural strength of 105 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 65 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 65 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 40 J Show Supplier Material materials with Instrumented Impact, Total Energy of 40 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 52 MPa Show Supplier Material materials with Tensile strength of 52 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.45E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.45E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.75E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 109 °C Show Supplier Material materials with Heat deflection temperature of 109 °C | ||||
Heat deflection temperature, 1.80 MPa | 109 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 109 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 95 °C Show Supplier Material materials with Relative temperature index, electrical of 95 °C | UL 746B | |||
Relative temperature index, mechanical impact | 95 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 95 °C | UL 746B | |||
Relative temperature index, mechanical strength | 95 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 95 °C | UL 746B | |||
Vicat softening temperature | 132 °C Show Supplier Material materials with Vicat softening temperature of 132 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥2.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101091262- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Supplier Material materials with Comparative tracking index of 3 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm | ≥, UL 746A | PLC 3 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15 g/10min Show Supplier Material materials with Melt mass-flow rate of 15 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Melt volume-flow rate | 15 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 15 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Power Manangement, Document Handling, Circuit Protection, Building Accessory, Freezer, EV/HEV Battery, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 95 to 100.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |