NORYL™ Resin CN1134 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ CN1134 resin is a 20% filled blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high modulus, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm. NORYL CN1134 resin exhibits good dimensional stability, low moisture absorption, and high rigidity. It is an excellent candidate for printer chassis and electric vehicle battery (EV) applications.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.23 [-]

Show Supplier Material materials with Relative density of 1.23 [-]

ASTM D 792

Water absorption

23.0 °C

0.07 %

Show Supplier Material materials with Water absorption of 0.07 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

SABIC - Japan Method | break

Flexural modulus

23.0 °C

5.88 GPa

Show Supplier Material materials with Flexural modulus of 5.88 GPa

ASTM D 790

Flexural strength

23.0 °C

137 MPa

Show Supplier Material materials with Flexural strength of 137 MPa

ASTM D 790

Impact strength, Izod notched

23.0 °C

68 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 68 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

68 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 68 J/m

ASTM D 256

Tensile strength

23.0 °C

98 MPa

Show Supplier Material materials with Tensile strength of 98 MPa

SABIC - Japan Method | yield

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.5E-5 - 3.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 - 3.5E-5 1/K

TMA | -30°C to 30°C

Heat deflection temperature

106 °C

Show Supplier Material materials with Heat deflection temperature of 106 °C

Heat deflection temperature, 1.80 MPa

106 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 106 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

65 °C

Show Supplier Material materials with Relative temperature index, electrical of 65 °C

UL 746B

Relative temperature index, mechanical impact

65 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C

UL 746B

Relative temperature index, mechanical strength

65 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C

UL 746B

Flammability

UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228541- -

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

22.1 g/10min

Show Supplier Material materials with Melt mass-flow rate of 22.1 g/10min

ASTM D 1238 | 300°C/2.16 kgf

Shrinkage

23.0 °C

0.25 %

Show Supplier Material materials with Shrinkage of 0.25 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

EV/HEV Battery

Availability

Asia

Features

Hydrolytic Stability, Low Creep Sensitivity, Flame Retardant, Good Stiffness, Non-Halogenated, Non-Chlorinated, Non-Brominated, Low Warpage, Structural

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.