NORYL PPX™ Resin PPX7115 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 7115 resin is a non-reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade exhibits high modulus, high-temperature performance, excellent melt strength, impact resistance, hydrolytic and dimensional stability. NORYL PPX7115 resin is an excellent candidate for applications requiring high modulus and chemical resistance.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.37 GPa

Show Supplier Material materials with Elastic modulus of 1.37 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

5 %

Show Supplier Material materials with Elongation of 5 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

1.52 GPa

Show Supplier Material materials with Flexural modulus of 1.52 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

51 MPa

Show Supplier Material materials with Flexural strength of 51 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Tensile strength

23.0 °C

35 MPa

Show Supplier Material materials with Tensile strength of 35 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

83 - 114 °C

Show Supplier Material materials with Heat deflection temperature of 83 - 114 °C

Heat deflection temperature, 0.45 MPa

114 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 114 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

83 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 83 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

80 °C

Show Supplier Material materials with Vicat softening temperature of 80 °C

ISO 306 | Rate B/50

Technological properties

Property
Application areas

Pipe/Fitting

Availability

Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Low Warpage, High Impact Resistance

Processing methods

Middle - Zone 2 Temperature: 240 to 285.0°C
Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 250 to 290.0°C
Hopper Temperature: 60 to 80.0°C
Drying Time: 2 to 4.0hrs
Rear - Zone 1 Temperature: 225 to 275.0°C
Melt Temperature: 260 to 290.0°C
Drying Temperature: 60 to 65.0°C
Nozzle Temperature: 260 to 290.0°C
Mold Temperature: 40 to 60.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.