NORYL™ Resin NH4030B - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NH4030B resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high flow, injection moldable and extrusion grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm along with lower smoke production upon burning and low specific gravity for light-weight parts. NORYL NH4030B resin may be an excellent candidate for rail interior, electrical conduit, cable management, and ceiling-mounted electric applications.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.11 g/cm³

Show Supplier Material materials with Density of 1.11 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.04 %

Show Supplier Material materials with Moisture absorption of 0.04 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.11 [-]

Show Supplier Material materials with Relative density of 1.11 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.27 %

Show Supplier Material materials with Water absorption of 0.27 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.43 GPa

Show Supplier Material materials with Elastic modulus of 2.43 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

4 %

Show Supplier Material materials with Elongation of 4 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.38 GPa

Show Supplier Material materials with Flexural modulus of 2.38 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

90 MPa

Show Supplier Material materials with Flexural strength of 90 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

19 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 19 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

200 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 200 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

46 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 46 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

54 MPa

Show Supplier Material materials with Tensile strength of 54 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

8.39E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 8.39E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8.54E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.54E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

107 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 107 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

127 °C

Show Supplier Material materials with Vicat softening temperature of 127 °C

ISO 306 | Rate B/50

Flammability

Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Vertical Burn a (60s, 1.52mm) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 29- ASTM E 662 <br> Vertical Burn b (12s, 1.52mm) passes at: 4sec FAR 25.853 <br> NBS Smoke Density, Flaming, 20 min (3.2 mm): 126- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (3.2 mm): 35- ASTM E 662 <br> Draeger Tube Toxicity, Non-Flaming (1.52mm): Pass- AITM 3.0005, ABD0031 <br> Draeger Tube Toxicity, Flaming (1.52mm): Pass- AITM 3.0005, ABD0031 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100880699- -

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

42.7 g/10min

Show Supplier Material materials with Melt mass-flow rate of 42.7 g/10min

ASTM D 1238 | 300°C/5.0 kgf

Melt volume-flow rate

41 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 41 cm³/10min

ISO 1133 | MVR at 300°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Displays, Air Conditioning, Air Cabin Interiors, Vending Machine, Rail Cabin Interiors, Rail Seating, Rail, Interior Rail Components

Availability

Europe,Asia,Americas

Features

Hydrolytic Stability, Low Smoke and Toxicity, Low Creep Sensitivity, Non-Halogenated, Non-Chlorinated, Non-Brominated, Low Warpage, Good Processability

Processing methods

Barrel - Zone 1 Temperature: 215 to 250.0°C
Die Temperature: 215 to 250.0°C
Front - Zone 3 Temperature: 250 to 290.0°C
Roll Stack Temp - Top: 90 to 150.0°C
Roll Stack Temp - Bottom: 90 to 150.0°C
Drying Time (Cumulative): 12hrs
Calibrator Temperature: 30 to 60.0°C
Shot to Cylinder Size: 30 to 70.0%
Drying Time (Cumulative): 12hrs
Barrel - Zone 4 Temperature: 215 to 250.0°C
Adapter Temperature: 215 to 250.0°C
Maximum Moisture Content: 0.07%
Drying Time: 2 to 4.0hrs
Barrel - Zone 1 Temperature: 215 to 250.0°C
Hopper Temperature: 80 to 120.0°C
Water Bath Temperature: 30 to 50.0°C
Barrel - Zone 3 Temperature: 215 to 250.0°C
Barrel - Zone 2 Temperature: 215 to 250.0°C
Roll Stack Temp - Middle: 90 to 150.0°C
Drying Temperature: 95 to 105.0°C
Middle - Zone 2 Temperature: 240 to 280.0°C
Melt Temperature: 215 to 250.0°C
Die Temperature: 215 to 250.0°C
Mold Temperature: 65 to 100.0°C
Vent Depth: 0.038 to 0.051mm
Adapter Temperature: 215 to 250.0°C
Nozzle Temperature: 260 to 290.0°C
Back Pressure: 0.3 to 0.7MPa
Barrel - Zone 2 Temperature: 215 to 250.0°C
Drying Temperature: 95 to 105.0°C
Screw Speed: 20 to 100.0rpm
Rear - Zone 1 Temperature: 225 to 275.0°C
Maximum Moisture Content: 0.07%
Drying Time: 2 to 4.0hrs
Drying Time: 2 to 4.0hrs
Melt Temperature: 215 to 250.0°C
Maximum Moisture Content: 0.07%
Barrel - Zone 4 Temperature: 215 to 250.0°C
Barrel - Zone 3 Temperature: 215 to 250.0°C
Drying Time (Cumulative): 12hrs
Melt Temperature: 260 to 290.0°C
Drying Temperature: 95 to 105.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.