NORYL™ Resin LS6010 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ LS6010 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high performance, injection moldable and extrudable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm. NORYL LS6010 resin features low smoke production upon burning, high heat resistance, very low specific gravity, enhanced resistance to melting and dripping and meets the requirements of FAR 25.853. In addition, this material is heat stabilized and impact modified. It is an excellent candidate for aerospace interior applications such as rub strips, seat track covers, cable guides, switch panels, conduit, wall/ceiling mounted electronics, and parts machined from slab stock.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Railway

Aerospace

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.11 g/cm³ Show Supplier Material materials with Density of 1.11 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.11 [-] Show Supplier Material materials with Relative density of 1.11 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.2 % Show Supplier Material materials with Water absorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	8.3 % Show Supplier Material materials with Elongation of 8.3 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	100 MPa Show Supplier Material materials with Flexural strength of 100 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	18 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 18 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m	ASTM D 256 \| notched, -30°C
Instrumented Impact, Total Energy	23.0 °C	52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	58 MPa Show Supplier Material materials with Tensile strength of 58 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		124 °C Show Supplier Material materials with Heat deflection temperature of 124 °C
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		146 °C Show Supplier Material materials with Vicat softening temperature of 146 °C	ISO 306 \| Rate B/120
Flammability	Vertical Burn b (12s, 1.52mm) passes at: 4sec FAR 25.853 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> Vertical Burn a (60s, 1.52mm) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Draeger Tube Toxicity, Non-Flaming (1.52mm): Pass- Based on ASTM E 662 <br> Draeger Tube Toxicity, Flaming (1.52mm): Pass- Based on ASTM E 662

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		5.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 5.6 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate		5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Air Cabin Interiors, Aerospace, Aircraft Seating, Interior Rail Components
Availability	Europe,Asia,Americas
Processing methods	Drying Time (Cumulative): 12hrs Drying Temperature: 95 to 105.0°C Calibrator Temperature: 30 to 60.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Barrel - Zone 2 Temperature: 220 to 260.0°C Mold Temperature: 65 to 100.0°C Adapter Temperature: 220 to 260.0°C Barrel - Zone 3 Temperature: 220 to 260.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Roll Stack Temp - Bottom: 90 to 150.0°C Nozzle Temperature: 295 to 305.0°C Front - Zone 3 Temperature: 295 to 305.0°C Water Bath Temperature: 30 to 50.0°C Adapter Temperature: 220 to 260.0°C Maximum Moisture Content: 0.07% Die Temperature: 220 to 260.0°C Roll Stack Temp - Middle: 90 to 150.0°C Hopper Temperature: 80 to 120.0°C Drying Temperature: 95 to 105.0°C Roll Stack Temp - Top: 90 to 150.0°C Maximum Moisture Content: 0.07% Drying Time: 2 to 4.0hrs Drying Time (Cumulative): 12hrs Drying Time: 2 to 4.0hrs Barrel - Zone 3 Temperature: 220 to 260.0°C Melt Temperature: 220 to 260.0°C Screw Speed: 40 to 80.0rpm Barrel - Zone 2 Temperature: 220 to 260.0°C Drying Temperature: 95 to 105.0°C Shot to Cylinder Size: 30 to 70.0% Melt Temperature: 220 to 260.0°C Drying Time: 2 to 4.0hrs Rear - Zone 1 Temperature: 280 to 295.0°C Melt Temperature: 280 to 305.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Die Temperature: 220 to 260.0°C Middle - Zone 2 Temperature: 290 to 300.0°C Drying Time (Cumulative): 12hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.