NORYL GTX™ Resin GTX918W - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 918W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, and high melt flow. NORYL GTX918W resin may be an excellent candidate for automotive under-the-hood and electrical applications requiring the retention of properties while under thermal load.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Interior

Construction

Water Management

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	53 % Show Supplier Material materials with Elongation of 53 %	ASTM D 638 \| brk, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	98 MPa Show Supplier Material materials with Flexural strength of 98 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	202 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 202 kJ/m²	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	62 MPa Show Supplier Material materials with Tensile strength of 62 MPa	ASTM D 638 \| yld, Type I, 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	188 °C Show Supplier Material materials with Heat deflection temperature of 188 °C
Heat deflection temperature, 0.45 MPa	188 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 188 °C	ASTM D 648 \| 3.2 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	1.6 % Show Supplier Material materials with Shrinkage of 1.6 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Electronic Components, Console, Cooking Range, Auto Electrical, Circuit Protection, Meter Gas
Availability	Europe,Asia,Americas
Processing methods	Front - Zone 3 Temperature: 265 to 295.0°C Mold Temperature: 65 to 95.0°C Melt Temperature: 270 to 295.0°C Shot to Cylinder Size: 30 to 50.0% Drying Time (Cumulative): 8hrs Nozzle Temperature: 270 to 295.0°C Vent Depth: 0.013 to 0.038mm Maximum Moisture Content: 0.07% Drying Temperature: 95 to 105.0°C Middle - Zone 2 Temperature: 260 to 295.0°C Back Pressure: 0.3 to 1.4MPa Screw Speed: 20 to 100.0rpm Minimum Moisture Content: 0.02% Drying Time: 3 to 4.0hrs Rear - Zone 1 Temperature: 255 to 295.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.