NORYL GTX™ Resin GTX918W - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 918W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, and high melt flow. NORYL GTX918W resin may be an excellent candidate for automotive under-the-hood and electrical applications requiring the retention of properties while under thermal load.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

53 %

Show Supplier Material materials with Elongation of 53 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

2.4 GPa

Show Supplier Material materials with Flexural modulus of 2.4 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

98 MPa

Show Supplier Material materials with Flexural strength of 98 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

202 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 202 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

62 MPa

Show Supplier Material materials with Tensile strength of 62 MPa

ASTM D 638 | yld, Type I, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

188 °C

Show Supplier Material materials with Heat deflection temperature of 188 °C

Heat deflection temperature, 0.45 MPa

188 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 188 °C

ASTM D 648 | 3.2 mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.3 %

Show Supplier Material materials with Shrinkage of 1.3 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components, Console, Cooking Range, Auto Electrical, Circuit Protection, Meter Gas

Availability

Europe,Asia,Americas

Processing methods

Shot to Cylinder Size: 30 to 50.0%
Nozzle Temperature: 270 to 295.0°C
Drying Time: 3 to 4.0hrs
Vent Depth: 0.013 to 0.038mm
Mold Temperature: 65 to 95.0°C
Drying Time (Cumulative): 8hrs
Screw Speed: 20 to 100.0rpm
Front - Zone 3 Temperature: 265 to 295.0°C
Back Pressure: 0.3 to 1.4MPa
Drying Temperature: 95 to 105.0°C
Middle - Zone 2 Temperature: 260 to 295.0°C
Maximum Moisture Content: 0.07%
Minimum Moisture Content: 0.02%
Melt Temperature: 270 to 295.0°C
Rear - Zone 1 Temperature: 255 to 295.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.