General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.12 g/cm³ Show Supplier Material materials with Density of 1.12 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.12 [-] Show Supplier Material materials with Relative density of 1.12 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 4 % Show Supplier Material materials with Water absorption of 4 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.9 GPa Show Supplier Material materials with Elastic modulus of 2.9 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 12 % Show Supplier Material materials with Elongation of 12 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 95 MPa Show Supplier Material materials with Flexural strength of 95 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 70 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 52 MPa Show Supplier Material materials with Tensile strength of 52 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ball Pressure Test | PASS | IEC 60695-10-2 | 125°C +/- 2°C | |
Coefficient of thermal expansion | 23.0 °C | 8.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.3E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature | 191 °C Show Supplier Material materials with Heat deflection temperature of 191 °C | ||
Heat deflection temperature, 0.45 MPa | 191 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 191 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Specific heat capacity | 23.0 °C | 1.4E-3 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1.4E-3 J/(kg·K) | ASTM C 351 |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K) | ASTM C177 |
Vicat softening temperature | 197 °C Show Supplier Material materials with Vicat softening temperature of 197 °C | ISO 306 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 4000 Ω·cm Show Supplier Material materials with Volume resistivity of 4000 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 7.8 g/10min Show Supplier Material materials with Melt mass-flow rate of 7.8 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Melt volume-flow rate | 7 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg | |
Shrinkage | 23.0 °C | 1.3 % Show Supplier Material materials with Shrinkage of 1.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Head Protection, Circuit Protection | |
Availability | Europe,Asia,Americas | |
Processing methods | Barrel - Zone 3 Temperature: 245 to 260.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |