NORYL PPX™ Resin PPX7200U - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 7200U resin is a non-reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This UV-stabilized, injection moldable grade exhibits improved chemical resistance and surface aesthetics along with high-temperature performance, excellent melt strength, modulus, impact resistance, hydrolytic and dimensional stability. NORYL PPX7200U resin is an excellent candidate for applications such as hot water tank components and outdoor housings and enclosures.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

0.99 g/cm³

Show Supplier Material materials with Density of 0.99 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.7 GPa

Show Supplier Material materials with Elastic modulus of 1.7 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

115 %

Show Supplier Material materials with Elongation of 115 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

1.6 GPa

Show Supplier Material materials with Flexural modulus of 1.6 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

48 MPa

Show Supplier Material materials with Flexural strength of 48 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Charpy unnotched

23.0 °C

80 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m²

ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod notched

23.0 °C

14 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 14 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Tensile strength

23.0 °C

28 MPa

Show Supplier Material materials with Tensile strength of 28 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

9.9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9.9E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

1.08E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.08E-4 1/K

ASTM E 831 | -40°C to 40°C

Vicat softening temperature

107 °C

Show Supplier Material materials with Vicat softening temperature of 107 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

18 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 18 cm³/10min

ISO 1133 | MVR at 260°C/5.0 kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosure/Housing/Cover

Availability

Americas

Processing methods

Drying Temperature: 60 to 65.0°C
Drying Time: 2 to 4.0hrs
Maximum Moisture Content: 0.02%
Middle - Zone 2 Temperature: 240 to 280.0°C
Back Pressure: 0.3 to 0.7MPa
Front - Zone 3 Temperature: 250 to 290.0°C
Screw Speed: 20 to 100.0rpm
Drying Time (Cumulative): 8hrs
Vent Depth: 0.038 to 0.051mm
Shot to Cylinder Size: 30 to 70.0%
Melt Temperature: 260 to 290.0°C
Mold Temperature: 30 to 50.0°C
Nozzle Temperature: 260 to 290.0°C
Rear - Zone 1 Temperature: 225 to 275.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.