NORYL™ Resin ENG265F - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ ENG265F resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This material is suitable for profile extrusion and exhibits very good hydrolytic stability, low moisture absorption, good dimensional stability. NORYL ENG265F resin certifies to NSF 61 and is an excellent candidate for water management applications such as extruded tubes for reverse osmosis systems.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.06 [-]

Show Supplier Material materials with Relative density of 1.06 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.06 %

Show Supplier Material materials with Water absorption of 0.06 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.55 GPa

Show Supplier Material materials with Elastic modulus of 2.55 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3.1 %

Show Supplier Material materials with Elongation of 3.1 %

ISO 527 | yield

Flexural modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Flexural modulus of 2.5 GPa

ISO 178

Flexural strength

23.0 °C

95 MPa

Show Supplier Material materials with Flexural strength of 95 MPa

ISO 178

Gardner Impact

23.0 °C

5 J

Show Supplier Material materials with Gardner Impact of 5 J

ASTM D 3029 | -40°C

Hardness, Rockwell R

23.0 °C

119 [-]

Show Supplier Material materials with Hardness, Rockwell R of 119 [-]

ASTM D 785

Impact strength, Charpy notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/2C | 23°C

Impact strength, Izod notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

114 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 114 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

39 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 39 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

50 MPa

Show Supplier Material materials with Tensile strength of 50 MPa

ISO 527 | break

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.94E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.94E-5 1/K

ASTM E 831 | -40°C to 95°C

Heat deflection temperature

126 - 132 °C

Show Supplier Material materials with Heat deflection temperature of 126 - 132 °C

Heat deflection temperature, 0.45 MPa

132 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 132 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

126 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 126 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

90 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 90 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Vicat softening temperature

141 °C

Show Supplier Material materials with Vicat softening temperature of 141 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221150- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

3 V

Show Supplier Material materials with Comparative tracking index of 3 V

UL 746A | (UL) {PLC}

Dielectric constant, 60Hz

23.0 °C

2.65 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 2.65 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

19.7 kV/mm

Show Supplier Material materials with Dielectric strength of 19.7 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor, 50Hz

23.0 °C

4E-4 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 4E-4 [-]

ASTM D 150 | 50/60 Hz

High Amp Arc Ignition

23.0 °C

6 mm

Show Supplier Material materials with High Amp Arc Ignition of 6 mm

≥, UL 746A | PLC 4

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

6 mm

Show Supplier Material materials with Hot-Wire Ignition of 6 mm

≥, UL 746A | PLC 4

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

8.5 g/10min

Show Supplier Material materials with Melt mass-flow rate of 8.5 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

8 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Pipe/Fitting

Availability

Americas

Features

Hydrolytic Stability, Low Creep Sensitivity, Low Warpage, Food Contact Acceptable

Processing methods

Adapter Temperature: 250°C
Drying Time (Cumulative): 8hrs
Barrel - Zone 2 Temperature: 205°C
Melt Temperature: 225 to 255.0°C
Maximum Moisture Content: 0.02%
Die Temperature: 250°C
Barrel - Zone 4 Temperature: 225°C
Drying Temperature: 105 to 115.0°C
Barrel - Zone 3 Temperature: 225°C
Barrel - Zone 1 Temperature: 205°C
Drying Time: 2 to 4.0hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.