General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ASTM D 638 | brk, Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 67 MPa Show Supplier Material materials with Flexural strength of 67 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Gardner Impact | 23.0 °C | 24 J Show Supplier Material materials with Gardner Impact of 24 J | ASTM D 3029 | -30°C |
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Supplier Material materials with Hardness, Rockwell R of 113 [-] | ASTM D 785 |
Impact strength, Izod notched | 23.0 °C | 389 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 389 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 160 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 160 J/m | ASTM D 256 | -40°C |
Tensile strength | 23.0 °C | 42 MPa Show Supplier Material materials with Tensile strength of 42 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.38E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.38E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Heat deflection temperature | 82 - 93 °C Show Supplier Material materials with Heat deflection temperature of 82 - 93 °C | ||||
Heat deflection temperature, 0.45 MPa | 93 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 93 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 82 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 82 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Flammability | UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥3mm UL 94 <br> Radiant Panel Listing: TRUE- UL Tested <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221153- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
Dielectric constant, 60Hz | 23.0 °C | 2.8 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.8 [-] | ASTM D 150 | 50/60 Hz |
Dielectric strength | 23.0 °C | 24.8 kV/mm Show Supplier Material materials with Dielectric strength of 24.8 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Dissipation factor, 1MHz | 23.0 °C | 3.5E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 3.5E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 4E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 4E-3 [-] | ASTM D 150 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Data Transfer, Rail Cabin Interiors, Rail Seating, Wiring Devices, Wireless Communications | |
Availability | Americas | |
Processing methods | Drying Time (Cumulative): 8hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |