NORYL GTX™ Resin NX0031 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ NX0031 resin is a non-reinforced alloy of PPE/PA. This conductive, injection moldable grade exhibits high heat resistance, excellent chemical resistance, and high impact resistance. NORYL NX0031 resin was designed for electrostatic painting and powder coating without the need for a conductive primer. This material can also be solvent painted and is an excellent for candidate for exterior, painted applications such as trim and fairings for outdoor vehicles, motorcycle, heavy truck, bus, personal watercraft, and marine. It is available only in black.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Consumer Goods

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.09 g/cm³ Show Supplier Material materials with Density of 1.09 g/cm³	ISO 1183
Moisture absorption	23.0 °C	1.2 % Show Supplier Material materials with Moisture absorption of 1.2 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.09 [-] Show Supplier Material materials with Relative density of 1.09 [-]	ASTM D 792
Water absorption	23.0 °C	4.2 % Show Supplier Material materials with Water absorption of 4.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2 GPa Show Supplier Material materials with Elastic modulus of 2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	4 % Show Supplier Material materials with Elongation of 4 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	1.9 GPa Show Supplier Material materials with Flexural modulus of 1.9 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	75 MPa Show Supplier Material materials with Flexural strength of 75 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	18 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	20 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	224 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 224 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	42 J Show Supplier Material materials with Instrumented Impact, Total Energy of 42 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	50 MPa Show Supplier Material materials with Tensile strength of 50 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1E-4 1/K	ISO 11359-2 \| 23°C to 60°C
Coefficient of thermal expansion, transverse	23.0 °C	9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Heat deflection temperature		136 - 176 °C Show Supplier Material materials with Heat deflection temperature of 136 - 176 °C
Heat deflection temperature, 0.45 MPa		176 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 176 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa		136 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 136 °C	ASTM D 648 \| 3.2mm, unannealed
Vicat softening temperature		180 °C Show Supplier Material materials with Vicat softening temperature of 180 °C	ISO 306 \| Rate B/120
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=533883- - <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		8 g/10min Show Supplier Material materials with Melt mass-flow rate of 8 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate		8 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg
Shrinkage	23.0 °C	1.3 % Show Supplier Material materials with Shrinkage of 1.3 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Neighborhood Electric Vehicle, Motorcycle
Availability	Americas
Processing methods	Drying Time: 3 to 4.0hrs Drying Temperature: 95 to 105.0°C Back Pressure: 0.3 to 1.4MPa Front - Zone 3 Temperature: 265 to 295.0°C Shot to Cylinder Size: 30 to 50.0% Drying Time (Cumulative): 8hrs Melt Temperature: 270 to 295.0°C Mold Temperature: 65 to 95.0°C Rear - Zone 1 Temperature: 255 to 295.0°C Vent Depth: 0.013 to 0.038mm Screw Speed: 20 to 100.0rpm Middle - Zone 2 Temperature: 260 to 295.0°C Minimum Moisture Content: 0.02% Maximum Moisture Content: 0.07% Nozzle Temperature: 270 to 295.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.