NORYL PPX™ Resin PPX7115F - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 7115F resin is a non-reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This FDA certified injection moldable grade exhibits high impact resistance and good heat resistance along with hydrolytic and dimensional stability. NORYL PPX7115F resin is an excellent candidate for food contact applications requiring high impact, chemical resistance, and good heat performance.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

0.99 [-]

Show Supplier Material materials with Relative density of 0.99 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.37 GPa

Show Supplier Material materials with Elastic modulus of 1.37 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

75 %

Show Supplier Material materials with Elongation of 75 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

1.37 GPa

Show Supplier Material materials with Flexural modulus of 1.37 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

51 MPa

Show Supplier Material materials with Flexural strength of 51 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

534 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 534 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

534 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 534 J/m

ASTM D 256 | notched, 23°C

Instrumented Impact, Total Energy

23.0 °C

37 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 37 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

35 MPa

Show Supplier Material materials with Tensile strength of 35 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.62E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.62E-4 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

9.72E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9.72E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

112 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 112 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

85 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 85 °C

ASTM D 648 | 3.2mm, unannealed

Vicat softening temperature

131 °C

Show Supplier Material materials with Vicat softening temperature of 131 °C

ISO 306 | Rate A/50

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221243- -

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

14 g/10min

Show Supplier Material materials with Melt mass-flow rate of 14 g/10min

ASTM D 1238 | 260°C/5.0 kgf

Melt volume-flow rate

12 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min

ISO 1133 | MVR at 260°C/5.0 kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage, transverse of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Water Treatment/Filtration

Availability

Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Low Warpage, High Impact Resistance, Food Contact Acceptable

Processing methods

Screw Speed: 20 to 100.0rpm
Shot to Cylinder Size: 30 to 70.0%
Vent Depth: 0.038 to 0.051mm
Drying Time (Cumulative): 8hrs
Middle - Zone 2 Temperature: 240 to 280.0°C
Rear - Zone 1 Temperature: 225 to 275.0°C
Mold Temperature: 30 to 50.0°C
Melt Temperature: 260 to 290.0°C
Maximum Moisture Content: 0.02%
Back Pressure: 0.3 to 0.7MPa
Front - Zone 3 Temperature: 250 to 290.0°C
Nozzle Temperature: 260 to 290.0°C
Drying Time: 2 to 4.0hrs
Drying Temperature: 60 to 65.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.